Sintering Behavior and Microwave Dielectric Properties of LMZBS Glass Doped Li 3 Mg 4 NbO 8 Ceramics for LTCC Applications
Yichan Huang,Cheng Liu,Kui Liu,Dainan Zhang,Yuanxun Li,Huaiwu Zhang
DOI: https://doi.org/10.1007/s10854-023-11619-9
2023-01-01
Journal of Materials Science Materials in Electronics
Abstract:Li 3 Mg 4 NbO 8 ceramics with x wt% of Li 2 O–MgO–ZnO–B 2 O 3 –SiO 2 glass (Li 3 Mg 4 NbO 8 -LMZBS x , x = 0.5, 1.0, 1.5, 2.0, 4.0) were prepared by the traditional solid-state reaction method. Rietveld refinement and Raman spectra were adopted for crystal structure studies. Based on the experimental results, it is suggested that the permittivity ( ε r ) and the quality factor ( Q × f ) were mainly associated with the extrinsic factors; while the temperature coefficient of resonant frequency (τ f ) was inversely proportional to the octahedral distortion of Li–O bond and directly proportional to the octahedral distortion of Nb–O bond. Among all the specimens, the sample of x = 1.5 sintered at 950 °C for 5 h exhibited excellent microwave dielectric properties: ε r = 14.16 , Q × f = 109,704 GHz (at 9.6 GHz), τ f = − 31 ± 1 ppm/°C. In addition, good chemical compatibility between the ceramic matrix and Ag electrode also suggested that the Li 3 Mg 4 NbO 8 -LMZBS x ceramic system is potential for low temperature co-fired ceramics (LTCC) applications.