Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics
Lei Wen,Lue Wen-Zhong,Wang Xiao-Chuan,Liang Jun,Jiang Jian-Jun
DOI: https://doi.org/10.3724/SP.J.1077.2009.00957
IF: 1.292
2009-01-01
Journal of Inorganic Materials
Abstract:ZnAl2O4-Mg2TiO4-CaTiO3 ceramics were prepared by the solid-state reaction. The effects of CaTiO3 on phase compositions, microstructure and microwave dielectric properties were investigated. It shows that CaTiO3 can effectively improve the sinterability of the ceramics and lower the densification temperature by about 150 degrees C. ZnAl2O4-based spinel, CaTiO3, MgTi2O5 and Zn2Ti3O8 phases are included in the ZnA(2)O(4)-Mg2TiO4-CaTiO3 system, however, Zn2Ti3O8 phase disappears when the sintering temperature is higher than 1400 degrees C. As CaTiO3 content increases, CaTiO3 phase in the sintered body raises while MgTi2O5 phase reduces. Furthermore, CaTiO3 can adjust obviously the temperature coefficient of resonant frequency of the (1-x)ZnAl2O4-xMg(2)TiO(4)(x = 0.21) ceramics. When 6mol% CaTiO3 is added to the (1-x)ZnAl2O4--xMg(2)TiO(4) (x = 0.21) system, a temperature-stable microwave dielectric ceramics sintered at 1400 degrees C with an epsilon(r) of 11.8, a Q center dot f of 88080GHz and a tau(f) of - 7.8 x 10(-6)/degrees C can be obtained.