Abstract:CaO-doped BaZr0.05Ti0.95O3 (BZT) ceramics were prepared by the conventional solid state reaction rout, and the effects of CaO on phase composition, microstructure development and temperature-dependent dielectric properties were investigated. The phase composition was analyzed by XRD pattern, and the microstructures of the samples were observed by scanning electron microscopy (SEM), and their dielectric properties were measured at 1 kHz. The variation of dielectric properties at different sintering temperature was also discussed. The results of XRD test show that the main crystal phase of BZT based ceramics does not change obviously, and the perovskite structure is still present. However, with the increase of the amount of doping, some impurity phase will be produced. Microstructure analysis shows that the doping of calcium oxide to BZT can make the grain more compact and homogeneous. When BZT ceramics doped with CaO as 5 mol% and the sintering temperature is 1330 degrees C, the grain size is more uniform and the growth is better. With the increase of CaO contents the dielectric constant increased and reached a maximum value at 5mol%. The dielectric loss decrease with increasing CaO concentration, and the value of Tm is regularly shifted to lower temperature and broaden. Dielectric properties of doped samples were significantly modified.

Microwave Dielectric Properties of B<sub>2</sub>O<sub>3</sub> Doped Ca [(li<sub>1/3</sub>nb<sub>2/3</sub>)<sub>0.9</sub><sub>5</sub>zr<sub>0.0</sub><sub>5</sub>]o<sub>3</sub><sub>−δ &Lt;/sub>ceramics

Microwave Dielectric Properties of B<sub>2</sub>O<sub>3</sub> Doped Ca [(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.9</sub><sub>5</sub>Zr<sub>0.0</sub><sub>5</sub>]O<sub>3</sub><sub>−δ </sub>Ceramics

Effect of B<sub>2</sub>O<sub>3</sub> on Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3−δ</sub>−0.05TiO<sub>2</sub> Ceramics

Influence of sintered aid B2O3 on microwave dielectric properties of Ca[(Li1/3Nb2/3)0.95 Zr0.15]3+δ ceramics

Microwave dielectric properties of low-temperature sintered Ca[(Li 1/3Nb 2/3) 0.95Zr 0.05]O 3-δ-0.04TiO 2 ceramics

Crystal structure and microwave dielectric properties of Ca[(<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3</sub>−δ-xTiO<sub>2</sub> ceramics

Microwave Dielectric Properties of Low-Temperature Sintered Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.95</sub>Zr<sub>0.05</sub>]O<sub>3−δ</sub>−0.04TiO<sub>2</sub> Ceramics

Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3</sub><sub>−δ </sub>Ceramics with Glass Addition

Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.95</sub>Zr<sub>0.05</sub>]O<sub>3−δ−x</sub>TiO<sub>2</sub> Ceramics

Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.95</sub>Zr<sub>0.15</sub>]O<sub>3+δ</sub> Ceramics with Sm<sup>3+</sup> Substitution at A-Site

Effect of Glass Additions on Ca[(Li1/3Nb2/3)0.92Zr0.08]O3−δ Microwave Ceramics

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition

Effect of glass additions on Ca[(Li 1/3Nb 2/3) 0.92Zr 0.08]O 3-δ microwave ceramics

Microstructure and microwave dielectric properties of ZnO-B2O3 doped ceramics

Influence of ZnO-B<sub>2</sub>O<sub>3</sub>-Na<sub>2</sub>O Glass on Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.8</sub>Sn<sub>0.2</sub>]O<sub>3−δ</sub>−0.1TiO<sub>2</sub> Ceramics

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li(1/3)Nb(2/3))(0.8)Ti(0.2)]O(3-Delta) Ceramics With Znb(2)O(4) Glass Addition

Effect of ZrO 2 Doping on the Microwave Dielectric Properties of Ba(Mg 1/3 Nb 2/3 )O 3 Ceramics

Effect of B2O3 Doping on Microwave Dielectric Properties of (Zn0.5Mg0.5)Nb2O6 Ceramics

Effect of B_2O_3 Doping on Microwave Dielectric Properties of (Zn_(0.5)Mg_(0.5))Nb_2O_6 Ceramics

EFFECT OF DOPING IN LOW-TEMPERATURE SINTERING OF Ca[(Li1/3Nb2/3)0.8Ti0.2]O3-σ MICROWAVE DIELECTRIC CERAMICS

EFFECT OF DOPING CaO ON DIELECTRIC PROPERTIES OF BaZr0.05Ti0.95O3 CERAMICS