Abstract:In this study, (Cu1/3Nb2/3)(4+) complex cation and BaO-ZnO-B2O3 glass frit were adopted to solve the high sintering temperature and poor temperature stability of Ba3Nb4Ti4O21 ceramics. It is shown that pure Ba3Nb4Ti4O21 phase was formed when Ti site was partially replaced by (Cu1/3Nb2/3)(4+) cation. The increasing number of dopants decreases the dielectric polarizability, correspondingly, the dielectric constant and temperature coefficient of the resonance frequency values are reduced consistently. The variation of the Q x f value is determined by internal ionic packing fraction and external sintering densification. The (Cu1/3Nb2/3)(4+) cation effectively decreases the suitable sintering temperature from 1200 to 1050 degrees C while greatly improving the temperature stability. BaO-ZnO-B2O3 glass was used to further improve the low-temperature sintering characteristics of Ba3Nb4Ti4O21 ceramics. It is proven that the addition of glass frits effectively decreases the temperature to 925 degrees C with combinational excellent microwave dielectric properties: epsilon(r) similar to 55.6, Q x f similar to 5700 GHz, tau(f) similar to 3 ppm/degrees C, making the Ba3Nb4Ti4O21 ceramics promising in the applications of low-temperature cofired ceramic technology.

Effect of Glass Additions on Ca[(Li1/3Nb2/3)0.92Zr0.08]O3−δ Microwave Ceramics

Effect of glass additions on Ca[(Li 1/3Nb 2/3) 0.92Zr 0.08]O 3-δ microwave ceramics

Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3</sub><sub>−δ </sub>Ceramics with Glass Addition

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

Influence of ZnO-B<sub>2</sub>O<sub>3</sub>-Na<sub>2</sub>O Glass on Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.8</sub>Sn<sub>0.2</sub>]O<sub>3−δ</sub>−0.1TiO<sub>2</sub> Ceramics

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li(1/3)Nb(2/3))(0.8)Ti(0.2)]O(3-Delta) Ceramics With Znb(2)O(4) Glass Addition

Influence of Multi-Component Glass on Sintering Behavior and Microwave Properties of Zr Non-Stoichiometricly Substituted Ca[(Li1/3Nb2/3)]O3-δ Ceramic

Influence of sintered aid B2O3 on microwave dielectric properties of Ca[(Li1/3Nb2/3)0.95 Zr0.15]3+δ ceramics

Microwave dielectric properties of low-temperature sintered Ca[(Li 1/3Nb 2/3) 0.95Zr 0.05]O 3-δ-0.04TiO 2 ceramics

Microwave Dielectric Properties of B<sub>2</sub>O<sub>3</sub> Doped Ca [(li<sub>1/3</sub>nb<sub>2/3</sub>)<sub>0.9</sub><sub>5</sub>zr<sub>0.0</sub><sub>5</sub>]o<sub>3</sub><sub>−δ &Lt;/sub>ceramics

Effect of B<sub>2</sub>O<sub>3</sub> on Microwave Dielectric Properties of Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3−δ</sub>−0.05TiO<sub>2</sub> Ceramics

Microwave Dielectric Properties of Low-Temperature Sintered Ca[(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.95</sub>Zr<sub>0.05</sub>]O<sub>3−δ</sub>−0.04TiO<sub>2</sub> Ceramics

Crystal structure and microwave dielectric properties of Ca[(<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.92</sub>Zr<sub>0.08</sub>]O<sub>3</sub>−δ-xTiO<sub>2</sub> ceramics

Microwave Dielectric Properties of B<sub>2</sub>O<sub>3</sub> Doped Ca [(Li<sub>1/3</sub>Nb<sub>2/3</sub>)<sub>0.9</sub><sub>5</sub>Zr<sub>0.0</sub><sub>5</sub>]O<sub>3</sub><sub>−δ </sub>Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

EFFECT OF DOPING IN LOW-TEMPERATURE SINTERING OF Ca[(Li1/3Nb2/3)0.8Ti0.2]O3-σ MICROWAVE DIELECTRIC CERAMICS

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

Silver Co-Firable Zntinb2o8 Microwave Dielectric Ceramics With Li2o-Zno-B2o3 Glass Additive

(Cu1/3nb2/3)4+ Ionic Substituting Effects, Low-Temperature Sintering Behaviors, and Improved Temperature Stability of Ba3Nb4Ti4O21 Microwave Dielectric Ceramics

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass