Abstract:The (1 − x)(Li 0.03 Na 0.5 K 0.47 )(Nb 0.92 Sb 0.05 Ta 0.03 )O 3 –xBa 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (LNKNST–BCZT, x = 0, 0.5, 1.5, 2.5, and 3.5%) lead-free piezoceramics were synthesized by the conventional solid-state reaction method with adding nano-sized Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (BCZT) powder to investigate their influences on crystal structure and electrical properties. The X-ray diffraction (XRD) analysis reveals that all the sintered LNKNST–BCZT ceramics exhibit pure perovskite structure with the mainly rhombohedral (R) phase or the coexistence of rhombohedral (R) phase and tetragonal (T) phase. The composition of the LNKNST–1.5%BCZT ceramics locates around the critical point, i.e., the ceramics changing from the coexistence of rhombohedral (R) phase and tetragonal (T) phase to purely rhombohedral (R) phase, and presents the most densified microstructure morphology, which can be confirmed further by the field emission scanning electron microscope (FESEM) observation. There are two dielectric anomalies in the temperature dependent dielectric properties curves of the LNKNST–BCZT ceramics, which correlate with the ferroelectric rhombohedral (R) phase changing to the ferroelectric tetragonal (T) phase, and then to the paraelectric cubic (C) phase. Both the Curie–Weiss law and the power law fittings confirm the diffuse phase transition ferroelectrics characteristic of the LNKNST–1.5%BCZT ceramics, which is considered as correlating with the polar nanoregions (PNRs). Due to the densification effect caused by the chosen amount of nano-sized BCZT doping and the construction of R–T polymorphic phase boundary, the LNKNST–1.5%BCZT ceramics exhibit the best ferroelectric and piezoelectric properties. The complex impedance spectroscopy analysis confirms that the extrinsic electrical conduction mechanism at high temperatures is dominated by the oxygen vacancies induced by the evaporation of the alkali metals during sintering.

Influence of La–B–Zn Glass on the Sintering and Microwave Dielectric Properties of Ca–Nd–Ti Ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Low‐Fire Processing (ca1−xnd2x/3)tio3 Microwave Ceramics

Low-Fire Processing (Ca<sub>1−x</sub>Nd<sub>2x/3</sub>)TiO<sub>3</sub>Microwave Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Effects of nano-sized BCZT on structure and electrical properties of KNN-based lead-free piezoceramics

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

High dielectric constant perovskite ceramic sintered at low temperature with La–Li–Zn–B glass for LTCC applications

A synergistic effect of La2O3–B2O3–ZnO and V2O5–CuO glass on the low-temperature sintering of Ca0.6La0.268TiO3 dielectric ceramic

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li1/3nb2/3)(0.84)Ti-0.16]O3-Delta Ceramics for Ltcc Applications

Low Temperature Sintering and Microwave Dielectric Properties of Ba<sub>4</sub>Nd<sub>9.33</sub>Ti<sub>18</sub>O<sub>54</sub> Ceramics Doped with Crystallizable Glass

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass

Low-temperature sintering and dielectric properties of high-permittivity microwave (Ca, Nd)TiO 3 ceramics

Microwave dielectric properties of Ca0.7Nd0.2TiO3 ceramic-filled CaO-B2O3-SiO2 glass for LTCC applications

Sintering and Microwave Dielectric Properties of La(Mg0.5Ti0.5)O3 Ceramics Doped with La2O3–B2O3–TiO2 Glass

Microstructure and microwave dielectric properties of ZnO-B2O3 doped ceramics

Microwave dielectric properties of low-temperature-fired MgNb2O6 ceramics for LTCC applications

Low-temperature sintering kinetics and dielectric properties of Ba5Nb4O15 with B2O3–SiO2 glass

Low-Temperature Sintering and Microwave Dielectric Properties of Znzrnb2o8 Ceramics with Bacu(B2o5) Addition