Microwave dielectric properties of Li 2 O– x MgO–ZnO–B 2 O 3 –SiO 2 glass-ceramics ( x = 30–50 wt.%)
Linshan Xie,Chaowei Zhong,Zixuan Fang,Yu Zhao,Bin Tang,Shuren Zhang
DOI: https://doi.org/10.2109/jcersj2.17156
2018-01-01
Journal of the Ceramic Society of Japan
Abstract:High crystallization, low-dielectric-loss Li2O-xMgO-ZnO-B2O3-SiO2 x = 30, 35, 40, 45 and 50 wt.%) (LMZBS) glass-ceramics were prepared with different MgO contents using the solid-state method in this study. The effects of the MgO content on the microstructures, flexural strength and microwave dielectric properties of LMZBS were investigated. X-ray diffractometer results, for samples sintered at 920 degrees C, for 30 wt.% <= x <= 35 wt.%, showed that the main phase was Mg2B2O5 and the secondary phase was Li2ZnSiO4. But a new Mg3B2O6 phase appeared when the MgO content exceeded 35 wt.%, becoming the main phase at x = 50 wt.%. Scanning electron microscopy showed that the average grain size decreased with increases in MgO and that a compact, homogeneous microstructure could be obtained at x = 40 wt.%. The Q x f value product of qualify factor and resonant frequency) increased at first due to increases in the theoretical Q quality factor) value and relative density, and then decreased due to a decrease in the average grain size and the appearance of large amounts of the liquid phase. Finally, the Li2O-xMgO-ZnO-B2O3-SiO2 glass-ceramics with 40 wt.% MgO exhibited excellent microwave properties and mechanical properties in terms of dielectric constants (epsilon(r) = 6.66), Qxf = 54600 GHz, temperature coefficient of resonant frequency (tau(f) = (1) 35 ppm/degrees C) and flexural strength (sigma = 160MPa) after the samples were sintered at 920 degrees C for 2 h in air, indicating their suitability as low-temperature co-fired ceramics. (C) 2018 The Ceramic Society of Japan. All rights reserved.