Preparation and Characterization of Silica Fiber Reinforced Boron Modified Methyl Phenolic Resin Matrix Composites

Qinging Xu,Yunhui Li,Fanming Zeng,Pengyang Deng,Zhongmin Su,Hailiang Zhang,Ce Liang,Xinning Zhang,Zhengmeng Sun

DOI: https://doi.org/10.1109/ICAIT52638.2021.9702090

2021-01-01

Abstract:Methyl phenolic resin and boron modified methyl phenolic resin were synthesized by solution polymerization using m-cresol, formaldehyde and boric acid as raw materials, and quartz fiber reinforced resin matrix composites were prepared using the two resins as matrix. The structure of the resin was characterized, and its solubility, mechanical properties, heat resistance and ablative heat insulation properties of the composite were tested. The effect of resin structure on its properties was studied. Compared with methyl phenolic resin, boron modified phenolic resin not only has better solubility and mechanical properties, but also increases the initial decomposition temperature and peak decomposition temperature by 170°C, the carbon residue rate by 11.11%, and improves the ablative heat insulation performance of the composite. The linear ablative rate is 0.0003333 mm s-l, and the mass ablative rate is 0.0002733 g s-l, The back temperature of 4mm sheet is 110°C after 10 min of gas oxygen ablation, which is expected to be used as the matrix resin of thermal protection materials.