Abstract:Aimed at the problem of insufficient heat resistance and poor ablation resistance of phenolic resin (RF), and the compatibility of SiO2 particles with phenolic resin, the nano-scale SiO2/RF hybrid aerogel was prepared by the co-gel method. The interpenetrated gel network was constructed to increase the compatibility of two phases. The microstructure, chemical structure and thermophysical properties of the SiO2/RF hybrid aerogel were explored. The silica-modified phenolic/carbon fiber composite material was prepared. The ablation properties of the composite material before and after modification were compared. The results show that the hybrid aerogel possesses a bi-continuous structure of skeleton and pores. The density of the hybrid aerogel fluctuates in the range of 0.145-0.160 g/cm(3). As the silica content increases, the residual carbon ratio of the hybrid aerogel increases, and the Si-O bond absorption vibration peak is more obvious, but XRD has no diffraction peak. Considering the pore size distribution and thermal physical properties, the silica-modified phenolic/carbon fiber composite material was prepared with the best performance hybrid aerogel. The mass ablation rate of the modified composite material is 0.046 g/s, and the linear ablation rate is 0.074 mm/s. Compared with the unmodified composite material, the mass ablation rate is reduced by 20.7%, the linear ablation rate is reduced by 21.3%. The oxidation resistance and the residual carbon ratio of the modified material are significantly improved.

Glass fiber reinforced SiC hybrid environmentally friendly phenolic resin composite

Novel Silicon-Modified Phenolic Novolac Resins: Non-isothermal Curing Kinetics, and Mechanical and Thermal Properties of Their Biofiber-Reinforced Composites

Sustainable, Biobased Silicone with Layered Double Hydroxide Hybrid and Their Application in Natural-Fiber Reinforced Phenolic Composites with Enhanced Performance

Novel silicon-modified phenolic novolacs and their biofiber-reinforced composites: Preparation, characterization and performance

Preparation of glass fiber reinforced phenolic injection molding materials and its properties

Preparation of Magnesium Hydroxide Sulfate Whisker-Phenolic Resin Composite by In-Situ Polymerization Technique and Its Properties

Improved Thermal Stabilities, Ablation and Mechanical Properties for Carbon Fibers/Phenolic Resins Laminated Composites Modified by Silicon-containing Polyborazine

Environment friendly waste-water-free and thermally conductive phenolic resin modified with polysulfone

On preparation and properties of G-POSS/CE hybrid materials

Preparation and Characterization of Silica Fiber Reinforced Boron Modified Methyl Phenolic Resin Matrix Composites

Preparation and characterization of POSS‐SiO2/cyanate ester composites with high performance

Synthesis of Silicon Hybrid Phenolic Resins with High Si-Content and Nanoscale Phase Separation Structure

Silicone–acetylene Hybrid Resin and Composite

Preparation and Ablation Performance of Silica Modified Phenolic/carbon Fiber Composite

Preparation and flame retardancy of waterbased phenolic resin/silica hybrid material prepared by in situ polymerization

Synthesis and structure evolution of phenolic resin/silicone hybrid composites with improved thermal stability

Preparation and properties of SiC/SiOX heterojunction fiber reinforced porous SiC composite materials

Study of Phase Transition, Structure Modulation, and Thermal Properties of Si/B-modified Bisphenol a Phenolic Resin Ceramicizable Materials

Preparation and properties of silicon nitride/glass fiber/epoxy composites

The Oxidation of SiC Fiber and SiC Fiber Reinforced Boron Phenolic Resin Composite

Phenolic Resin Modified by Boron-Silicon with High Char Yield