Preparation and Ablation Performance of Silica Modified Phenolic/carbon Fiber Composite

Xu Pan,Shiyang Zhu,Yesheng Zhong,Mingwei Li,Liping Shi,Xiaodong He

DOI: https://doi.org/10.11868/j.issn.1001-4381.2021.000954

2023-01-01

Abstract:Aimed at the problem of insufficient heat resistance and poor ablation resistance of phenolic resin (RF), and the compatibility of SiO2 particles with phenolic resin, the nano-scale SiO2/RF hybrid aerogel was prepared by the co-gel method. The interpenetrated gel network was constructed to increase the compatibility of two phases. The microstructure, chemical structure and thermophysical properties of the SiO2/RF hybrid aerogel were explored. The silica-modified phenolic/carbon fiber composite material was prepared. The ablation properties of the composite material before and after modification were compared. The results show that the hybrid aerogel possesses a bi-continuous structure of skeleton and pores. The density of the hybrid aerogel fluctuates in the range of 0.145-0.160 g/cm(3). As the silica content increases, the residual carbon ratio of the hybrid aerogel increases, and the Si-O bond absorption vibration peak is more obvious, but XRD has no diffraction peak. Considering the pore size distribution and thermal physical properties, the silica-modified phenolic/carbon fiber composite material was prepared with the best performance hybrid aerogel. The mass ablation rate of the modified composite material is 0.046 g/s, and the linear ablation rate is 0.074 mm/s. Compared with the unmodified composite material, the mass ablation rate is reduced by 20.7%, the linear ablation rate is reduced by 21.3%. The oxidation resistance and the residual carbon ratio of the modified material are significantly improved.