Abstract:Experimental Overview: A molybdenum phenolic fiber has been developed.The synthetic solution was mixed with PVB, wet spinning, and then molybdenum phenolic fiber with better performance were obtained by four different curing methods. With the addition of molybdenum acid, the Mo‐o bond enters the molecular chain of high‐neighborhood phenolic fibers, which improves the cross‐linking degree and thermal stability. The study aims to produce thermosetting resin from synthesized molybdenum‐modified high‐ortho thermoplastic phenolic resin through an addition reaction. Then, molybdenum‐modified high‐ortho thermosetting phenolic resin is blended with polyvinyl butyral and undergoes wet spinning to prepare as‐spun fibers and obtain high‐ortho molybdenum phenolic fibers via solution curing, microwave curing, or heat curing. Fourier transform infrared spectroscopy, nuclear magnetic resonance, thermogravimetric analysis, scanning electron microscopy, and fiber strength testing were used to investigate the structure and properties of molybdenum‐modified high‐ortho phenolic fibers. Results showed that adding molybdic acid introduced Mo−O bonds into the molecular chain of high‐ortho phenolic resin, thereby improving the degree of cross‐linking and thermal stability. The residual carbon content of the fibers after heat treatment exceeded 60%, and the elongation at break and the breaking strength of the microwave‐cured fibers reached 4.2% and 155 MPa, respectively, and the mechanical properties were relatively good. The study of high‐ortho phenolic fibers aims to improve their properties and expand their applications through resin modifications. It provides a possible fiber preparation strategy for improving heat‐resistant phenolic fibers, thereby guiding the research of modified high‐ortho phenolic fibers.

Preparation of glass fiber reinforced phenolic injection molding materials and its properties

Preparation of Phenolic Injection Molding Materials with Excellent High Heat Stability of Appearance Characteristics

Novel Silicon-Modified Phenolic Novolac Resins: Non-isothermal Curing Kinetics, and Mechanical and Thermal Properties of Their Biofiber-Reinforced Composites

Study of Post-curing Properties of Wood Flour Reinforced Phenolic Molding Materials

Properties of Phenolic Molding Compounds Reinforced with Sisal Fiber

Preparation of Magnesium Hydroxide Sulfate Whisker-Phenolic Resin Composite by In-Situ Polymerization Technique and Its Properties

Development of an Injection Molding Process for Long Glass Fiber-Reinforced Phenolic Resins

Novel silicon-modified phenolic novolacs and their biofiber-reinforced composites: Preparation, characterization and performance

Preparation of high molecular weight thermoplastic bio-based phenolic resin and fiber based on lignin liquefaction

Preparation and Microwave Curing of Blended Phenolic Epoxy Fibers

Improved Thermal Stabilities, Ablation and Mechanical Properties for Carbon Fibers/Phenolic Resins Laminated Composites Modified by Silicon-containing Polyborazine

Investigation of the mechanical and flame retardant properties of carbon fiber modified phenolic epoxy resin

Structural Evolution of Phenolic Fibers during the Forming Process

Preparation and Properties of Molybdenum‐modified High‐ortho Thermosetting Phenolic Fiber

Mechanical and thermal properties of phenolic/glass fiber foam modified with phosphorus-containing polyurethane prepolymer

Preparation and properties of high-temperature resistant bisphthalonitrile resins containing trifluoromethyl groups reinforced by poly (aryl ether nitrile) capped by phthalonitrile and composites

Preparation of a Ceramifiable Phenolic Foam and Its Ceramization Behavior

Study of Phase Transition, Structure Modulation, and Thermal Properties of Si/B-modified Bisphenol a Phenolic Resin Ceramicizable Materials

Preparation and properties of epoxy-modified thermosetting phenolic fiber

Effects of Heating and Cooling of Injection Mold Cavity Surface and Melt Flow Control on Properties of Carbon Fiber Reinforced Semi-Aromatic Polyamide Molded Products

Study on the Curing Behavior of Polythiol/phenolic/epoxy Resin and the Mechanical and Thermal Properties of the Composites