Abstract:This work presents the results of research on the influence of the amount of p-toluenesulfonic acid and phosphoric acid (V) added to the phenol-formaldehyde resin (pH 7.3–7.8) on its thermal properties and on the phenol-formaldehyde-carbon composite produced on its basis. This material undergoes pyrolysis under high temperature. The addition of a catalyst to the phenol-formaldehyde resin affects its curing rate and degree of cross-linking, but how it affects the thermal properties of the resin depending on the temperature is the subject of this work. This article presents the results of thermal tests for phenol-formaldehyde resin and phenol-formaldehyde-carbon composite. It was examined how the content of the catalyst used during the production process affects the individual thermal parameters of the mentioned materials. The results include experimental tests of thermal diffusivity with uncertainty (±3%), specific heat capacity (±2.5%), thermal expansion with resolution 2 nm analyzed in the temperature range −40–115 °C and thermogravimetric TG/DTA analysis with resolution 0.03 μg in the temperature range from room temperature (RT = 23 °C) to 550 °C. Individual thermal tests showed changes in the thermal properties caused by changes in the catalyst content of the tested materials and the influence of the addition of carbon fibers on the properties of the composite compared to the pure phenol-formaldehyde resin. It was found that there is a certain maximum level of catalyst weight fraction at which the greatest decrease in thermal diffusivity occurs. In the case of phenolic-formaldehyde-carbon composite at −40 °C, an increase in catalyst weight fraction from 2 to 4 wt% caused a decrease in thermal diffusivity by 18.2%, and for phenol-formaldehyde resin, it was 2.8% with an increase in catalyst fraction from 4 to 10 wt%.

Study on the Curing Behavior of Polythiol/phenolic/epoxy Resin and the Mechanical and Thermal Properties of the Composites

Cure Kinetics of an Epoxy Resin Containing Naphthyl/dicyclopentadiene Moieties and Bis‐phenoxy (3‐hydroxy) Phosphine Oxide System and Properties of Its Cured Polymer

STUDY ON DGE-BHBTMBP/E-51/DDS CURED

Silicone-modified Phenolic Resin: Relationships Between Molecular Structure and Curing Behavior

Curing Kinetics and the Properties of KH560-SiO2/Polyethersulfone/Bismaleimide-Phenolic Epoxy Resin Composite

Curing and pyrolysis behavior of PF/B4C/PBZ composite

Investigation on the Curing and Thermal Properties of Epoxy/Amine/Phthalonitrile Blend

Preparation and Microwave Curing of Blended Phenolic Epoxy Fibers

Investigation of the mechanical and flame retardant properties of carbon fiber modified phenolic epoxy resin

Cure Kinetics and Thermal Properties of Tetramethylbiphenyl Epoxy Resin/phthalazinone‐containing Diamine/hexa(phenoxy)cyclotriphophazene System

The curing kinetics and mechanical properties of epoxy resin composites reinforced by PEEK microparticles

The Effect of p-Toluenesulfonic Acid and Phosphoric Acid (V) Content on the Heat Resistance and Thermal Properties of Phenol Resin and Phenol-Carbon Composite

Study on Toughening of Matrix Resins for Advanced Composite

Curing kinetics and thixotropic properties of epoxy resin composites with different kinds of fillers

Promotion on the thermal and mechanical behaviors of epoxy resin using phthalonitrile and functionalized‐SiO2

Curing Behaviors and Properties of Epoxy and Self-Catalyzed Phthalonitrile with Improved Processability

Synthesis of Epoxy Resin Based on Biphenyl Structure for Application in Carbon Fiber-Reinforced Composites

Practical Technology of Toughening Epoxy Resin (II): Modification Effects of Special Engineering Plastics on Epoxy Resin

Hierarchical Curing Mechanism in Epoxy/bismaleimide Composites: Enhancing Mechanical Properties Without Compromising Thermal Stabilities

Curing Behaviors of Cyanate Ester/epoxy Copolymers and Their Dielectric Properties

Studies on the curing behavior, thermal, and mechanical properties of epoxy resin‐co‐amine‐functionalized lead phthalocyanine