Abstract:Despite the wealth of literature on the friction and wear behaviour of ceramics, their wear mechanisms are far from well understood. The need to develop a precise understanding of the wear mechanisms is imperative for the development of better wear-resistant ceramics. Particularly in alumina ceramics, grain coarsening has been found to improve the crack growth resistance characteristics. However, if the same would be beneficial for wear resistant applications has not been systematically investigated. To evaluate if there exists a strong grain size effect on abrasive wear mechanisms in ceramics, a series of tests were conducted under severe sliding contact conditions in an alumina ceramic. Unlubricated sliding wear tests were performed on alumina of three different grain sizes, 0.7, 5 and 25 μm, using a blunt conical diamond indenter of about 100-μm tip radius as the slider at room temperature under normal loads of 8–40 N and sliding distances up to 120 mm. The abrasive wear behaviour was characterised by measuring the wear volume and wear rate as a function of normal load and sliding distance. In addition, the friction behaviour was also studied simultaneously as a function of these two variables. The wear damage mechanisms were examined using both optical and electron microscopy as well as energy dispersive X-ray spectroscopy. For a given grain size and sliding distance, the width and depth of the worn track (hence wear volume) and the frictional force all increased with normal load. These observations were more markedly displayed in the coarse-grained than in the fine-grained alumina. In the 0.7-μm fine-grained alumina, the wear process appeared to be mainly controlled by plastic deformation especially at low loads (e.g. < 10 N). At higher loads, however, both plastic deformation and grain boundary fracture processes seemed to be involved. In the 5-μm and 25-μm coarse-grained aluminas, the predominant material removal process was controlled by both intergranular and transgranular fractures.

Size Effect of CeO2 Particle on Nanoscale Single-Asperity Sliding Friction

Exploring the Effect of Nanoparticle Size on the Tribological Properties of Sio2 / Polyalkylene Glycol Nanofluid under Different Lubrication Conditions

The Size Effect of SiO2 Particles on Friction Mechanisms of a Composite Friction Material

Grain size effect on abrasive wear mechanisms in alumina ceramics

Contact size effects on the friction and wear of amorphous carbon films

Nano-sized single-asperity friction behavior: Insight from molecular dynamics simulations

Micro-scale contact behavior and its effect on the material removal process during chemical mechanical polishing

Study on uniform size and spherical CeO 2 abrasives synthesized by two-step method and their chemical mechanical polishing performances

Influence of Cerium Oxide Abrasive Particle Morphologies on Polishing Performance

Mechanical wear behavior between CeO2(100), CeO2(110), CeO2(111), and silicon studied through atomic force microscopy

Study on Uniform Size and Spherical Ceo2 Abrasives Synthesized by Two-Step Method and Their Chemical Mechanical Polishing Performances

Tribological Properties of Nanometer Cerium Oxide As Additives in Lithium Grease

Tribological mechanism of micro/meso/macroscopic textured surfaces under different normal forces, relative velocities, and sliding directions

Micromechanics of Friction: Effects of Nanometre-Scale Roughness

Experimental Study on Polishing Performance of CeO2 and Nano-Sio2 Mixed Abrasive

Effect Of Surface Energy On Shearing Of Metal Asperities Contact At The Nanoscale

The effect of abrasive grain size on the transition between abrasive and adhesive wear

Tribological behavior anisotropy in sliding interaction of asperities on single-crystal α-iron: A quasi-continuum study

Effect of the Particle Size on Tribological Properties of Nanometer Fe3O4 as Lubricating Oil Additives

Effect of size distribution on the adhesion of nanoscale asperities

Effect of Grain Size on the Adhesive and Ploughing Friction Behaviours of Polycrystalline Metals in Forming Process