Abstract:Despite the wealth of literature on the friction and wear behaviour of ceramics, their wear mechanisms are far from well understood. The need to develop a precise understanding of the wear mechanisms is imperative for the development of better wear-resistant ceramics. Particularly in alumina ceramics, grain coarsening has been found to improve the crack growth resistance characteristics. However, if the same would be beneficial for wear resistant applications has not been systematically investigated. To evaluate if there exists a strong grain size effect on abrasive wear mechanisms in ceramics, a series of tests were conducted under severe sliding contact conditions in an alumina ceramic. Unlubricated sliding wear tests were performed on alumina of three different grain sizes, 0.7, 5 and 25 μm, using a blunt conical diamond indenter of about 100-μm tip radius as the slider at room temperature under normal loads of 8–40 N and sliding distances up to 120 mm. The abrasive wear behaviour was characterised by measuring the wear volume and wear rate as a function of normal load and sliding distance. In addition, the friction behaviour was also studied simultaneously as a function of these two variables. The wear damage mechanisms were examined using both optical and electron microscopy as well as energy dispersive X-ray spectroscopy. For a given grain size and sliding distance, the width and depth of the worn track (hence wear volume) and the frictional force all increased with normal load. These observations were more markedly displayed in the coarse-grained than in the fine-grained alumina. In the 0.7-μm fine-grained alumina, the wear process appeared to be mainly controlled by plastic deformation especially at low loads (e.g. < 10 N). At higher loads, however, both plastic deformation and grain boundary fracture processes seemed to be involved. In the 5-μm and 25-μm coarse-grained aluminas, the predominant material removal process was controlled by both intergranular and transgranular fractures.

The Size Effect of SiO2 Particles on Friction Mechanisms of a Composite Friction Material

Exploring the Effect of Nanoparticle Size on the Tribological Properties of Sio2 / Polyalkylene Glycol Nanofluid under Different Lubrication Conditions

Effect of Lubricating Condition on Tribological Properties of Nano-SiO2 Filled Polyamide Composite

The effect of the modification mechanism of SiO2 in resin‐based friction materials on the mechanical and tribological performance

The Effect of Silica Size on the Friction and Wear Behaviors of Polyimide/silica Hybrids by Sol–gel Processing

Size Effects of SiO2 Nanoparticles As Oil Additives on Tribology of Lubricant

The Influence of Sliding Speed on the Friction Behavior of Silica Surface

Particle size effects on efficiency of surface texturing in reducing friction

Effect Of Nano-Sio(2) On The Properties Of Cu-Base Friction Material

The Microstructure and Wear Characteristics of Cu–Fe Matrix Friction Material with Addition of SiC

Study on Friction Properties of Cu-Based Friction Materials with Ni Coated Nano-Sio2 Particles

Study on the effect of particle size and dispersion of SiO2 on tribological properties of nitrile rubber

Development of a Composite Friction Material with Excellent Fade Resistance by Employing Oversized Ceramic Particles

Tribological Behavior and Wear Mechanism of Cu-SiO2 Sintered Composite under Different Sliding Speeds

Frictional Behavior and Wear Mechanisms of Ag/MoS 2 /WS 2 Composite Under Reciprocating Microscale Sliding

Effects of Abrasive Particles on Liquid Superlubricity and Mechanisms for Their Removal

The effect of abrasive grain size on the transition between abrasive and adhesive wear

Contact size effects on the friction and wear of amorphous carbon films

Friction of the micron-scale silica under various behaviors of the shape and the orientation of the coarse-grained particle in adaptive smoothed particle hydrodynamics

Grain size effect on abrasive wear mechanisms in alumina ceramics

Dry Sliding Behavior and Particulate Emissions of a SiC-graphite Composite Friction Material Paired with HVOF-Coated Counterface