Abstract:The tribological behavior of the rheoformed and thixoformed nano-sized SiCp/7075 composite parts is investigated. The semisolid stirring temperature has a little influence on the friction coefficient and wear resistance of the rheoformed composite parts. As for the thixoformed composite parts, the average value of the steady-state coefficient of friction increases firstly and then decreases with increasing reheating temperature. Higher wear resistance is achieved at a reheating temperature of 580 degrees C. The average value of the steady-state friction coefficient of the rheoformed composite parts varies from 0.37 to 0.45 upon applied loads of from 20 to 50 N. Weight loss increases slightly upon an increase of applied load from 20 to 40 N. An applied load of 50 N leads to a significant increase of the weight loss. The wear rate decreases firstly and then increases with increasing applied load. As for the thixoformed composite part, the average value of the steady-state friction coefficient and the weight loss decreased with an increasing applied load. However, the wear rate decreases firstly with increasing applied load and then increases. As for the rheoformed composite part, the average value of the steady-state friction coefficient decreases firstly and then increases a little with increasing sliding velocity. Weight loss and wear rate show a first increase and a followed decrease with increasing sliding velocity. As for the thixoformed composite part, the average value of the steady-state friction coefficient shows a decrease with increasing sliding velocity. Weight loss and wear rate exhibit, at first, an increase, and then a decrease with increasing sliding velocity. The average friction coefficient varies from 0.4 to 0.44 with increasing volume fraction of SiC. Weight loss and wear rate decrease with increasing volume fraction of SiC. An increase in dislocation density around the nano-sized SiC particles and the mismatch of the coefficient of thermal expansion (CTE) between 7075 matrix and nano-sized SiC particles during solidification improve the wear resistance of the composite. The dominant wear mechanisms of the rheoformed and thixoformed composite parts are adhesive wear, abrasive wear and delamination wear.

The effect of the modification mechanism of SiO2 in resin‐based friction materials on the mechanical and tribological performance

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

The Performance of Resin-based Friction Material Modified by Calcium Silicate Particles

Tribological Properties of Bismaleimide Composites with Surface‐modified SiO2 Nanoparticles

Effect of Load on Frictional Property of Nano-meter SiC/BMI-BA Composite

Effects of surface modification of nano-SiO_2 on friction properties of Cu-based friction materials

Effect of Nano-Sio2 Particles on the Carbon Fabric/resin Friction Materials by Microwave-Hydrothermal Treatment

Significant Enhancement on the Mechanical and Tribological Performances of Paper‐based Friction Materials by Designing Silicone@sio2 Core‐shell Structure

Effect Of Nano-Sio(2) On The Properties Of Cu-Base Friction Material

Effects of Friction Film Mechanical Properties on the Tribological Performance of Ceramic Enhanced Resin Matrix Friction Materials

Study on the Friction and Wear Properties of Carbon Fabric Composites Reinforced with Micro- and Nano-Particles

Effects of Content of SiO_2 Particles on Tribological Behavior of Cu-matrix Friction Materials

Effect of interfacial interaction between Nano-SiO2 and NBR on tribological properties of NBR water-lubricated bearings

Friction and wear properties of carbon fabric composites filled with nano-Al2O3 and nano-Si3N4

Tribological Behavior of Nano-Sized SiCp/7075 Composite Parts Formed by Semisolid Processing

The Effect of Silane Coupling Agent on the Sliding Wear Behavior of Nanometer ZrO 2 /bismaleimide Composites

Influences of Surface Modification of Nano-Silica by Silane Coupling Agents on the Thermal and Frictional Properties of Cyanate Ester Resin

Dependence of Tribological Characteristics on Mechanical Properties and Phase Transformations of Zirconia-Based Composite Ceramics

Morphology and Tribological Behaviors of in Situ Polymerized Nano-Sio2/Polyacrylate Nanocomposites

Tribological and Mechanical Behaviours of Resin‐based Friction Materials Based on Microcrack Filling

A molecular dynamics study of 3C‐SiC/epoxy nanocomposite as a metal‐free friction material