Tribological Properties of Different-sized Copper Nanoparticles Employed as Lubricating Oil Additives Using MD Simulations and Experiments br
Ling Pan,Jinyang Guo,Guobin Lin
DOI: https://doi.org/10.11933/j.issn.1007-9289.20220615001
2023-01-01
China surface engineering
Abstract:An effective method of reducing friction and wear is through the addition of nanoparticles to lubricating oil. However, although many researchers have linked the tribological properties of nanoparticles to their intrinsic properties, very few have related the tribological properties to the coupling effect of the nanoparticle size and surface roughness. Thus, the effect of the particle size of Cu nanoparticle additives on its tribological properties was investigated in this study using simulations and experiments. A boundary lubrication system model with peaks and grooves was established, and molecular dynamics(MD) simulations were used to simulate the mechanical properties of five types of nanoparticles with different sizes under a stress and relative shear velocity between the two solid walls of 300 MPa and 5 m / s, respectively. The stress, wear, friction force, positive pressure, and friction heat on the friction surface was quantitatively calculated, and the friction coefficient of the lubricating oil containing the Cu nanoparticles was measured using a micro-scratch tester. The results showed that the Cu nanoparticles increased the friction coefficient when the asperity was small and during boundary lubrication, and reduced the friction coefficient when the asperity was large and during mixed lubrication. Particularly, when the ratio of the particle diameter to the groove depth D / h was in the range of 1.05-1.12, namely, when the nanoparticle diameter was slightly larger than the groove depth, the tribological performance of the lubricating oil was excellent, the friction and wear was low, and the oil film bearing capacity was optimal. The Von Mises stress nephogram of the metal revealed that when the ratio of the particle diameter to the groove depth D / h was 1.12, the maximum stress on the solid surface was 2.45x10(4) MPa, which appears in the direct contact area between the upper and lower contact surface, compared to the maximum stress on the solid surface of 31.2 GPa in the lubrication system without Cu nanoparticles. Additionally, the maximum stress on the solid surface was reduced by 21.40% using Cu nanoparticles, which means that the bearing capacity of the lubrication system can be improved using the Cu nanoparticles additive. A comparison of the wear quantity of different nanoparticle sizes showed that the wear of the lubrication system containing Cu nanoparticles was smaller than that of the lubrication system without Cu nanoparticles, which indicates that Cu nanoparticles can reduce the wear of the lubrication system. When the depth of the groove h was 2.14 nm, an increase in the Cu nanoparticle size caused a reduction in the wear quantity, and when the Cu nanoparticle diameter D was 2.45 nm, the wear of the lubrication system was reduced by 20.70% compared to that in the system without Cu nanoparticles. The temperature distribution of the lubrication system showed that the highest temperature appears on the Z-axis coordinate from 3.5 similar to 4.5 nm, which is where the upper and lower solid surfaces are closest; and in the lubrication system without Cu nanoparticles, the maximum temperature of the system was 336 K. Moreover, Cu nanoparticles can reduce the temperature of the contact zone, and an increase in the nanoparticle size results in a further decrease in the maximum temperature. When D / h > 1, the maximum temperature of the lubrication system during the shearing process was reduced to approximately 300 K. In the micro-scratch test, the friction coefficient of the lubricating oil containing Cu nanoparticles of different sizes was smaller than that of the pure base oil. When Ra = 50 nm, the friction coefficient of lubricants with a D = 50 nm was smaller than that with a D = 100 nm, and under a D = 50 nm, the friction coefficient of lubricants with Ra = 50 nm was smaller than that with Ra = 100 nm. This indicates that the particle size D and surface roughness Ra have a coupling effect on the lubrication performance. Finally, simulations and experiments were simultaneously employed to study the effect of the size of Cu nanoparticles additive on the tribological properties. Additionally, an MD simulation was used to compensate for the deficiencies of the test, and the test was used to verify the MD simulation to a certain extent. The results of the simulations and experiments mutually confirm that the surface roughness and nanoparticle size have a coupling effect on the tribological properties of lubricating oil, which provides a theoretical basis for the application of nanoparticles additives. Keywords: boundary lubrication; nanoparticle; surface roughness; molecular dynamics