Tribological and Mechanochemical Properties of Nanoparticle-Filled Polytetrafluoroethylene Composites under Different Loads

Weixuan Lv,Tingmei Wang,Qihua Wang,Kian Kun Yap,Fuzhi Song,Chao Wang

DOI: https://doi.org/10.3390/polym16070894

IF: 5

2024-03-26

Polymers

Abstract:For the tribological properties of nanoparticle-modified PTFE, a more comprehensive study has been conducted, but there is still some room for research on tribology behavior, tribofilm formation and structure evolution of polytetrafluoroethylene (PTFE) filled with α-Al2O3 and SiO2 nanoparticles during sliding against steel counterparts under different loads. At the same time, it establishes the linkage and mechanism between the maintenance of mechanical strength and the tribological application of polymers in service and provides corresponding scientific data and theoretical guidance for the long-lasting application of polymer lubrication materials. It is found that both composites exhibit good wear resistance across the pressure of 1 MPa to 10 MPa, with the α-Al2O3/PTFE composite demonstrating better performance stability compared to the SiO2/PTFE composite. The high wear resistance is attributed to the formation of tribofilms at the friction interface. For the α-Al2O3/PTFE, an island-like tribofilm is formed with a thickness ranging from 100 to 200 nm, while the tribofilm of the SiO2/PTFE composite is thinner, measuring approximately 50 to 100 nm, and manifests a striped pattern. The chemical composition, both at the surface and subsurface levels, as well as the morphology of the tribofilms, were studied using FTIR spectrometry, X-ray photoelectron spectroscopy (XPS), and FIB-TEM. It is found that the difference in thickness and microstructure of the tribofilms for the two composites is mainly due to the tribochemistry of the nanoparticles. The α-Al2O3 nanoparticle plays a "cohesion" role during the formation of the tribofilm, which facilitates the formation of a thicker, more uniform, and stronger adhered tribofilm on the metallic counterpart, making it more robust against higher shear stress.

polymer science

What problem does this paper attempt to address?

The paper attempts to address the following main issues:

1. **Research Background**:
- Polytetrafluoroethylene (PTFE), as an excellent solid lubricant material, has good chemical stability, but its high wear rate limits its use in pure polymer form in practical applications. To improve its friction reduction and wear resistance performance, various fillers are usually added.

2. **Specific Issues**:
- **Tribological Behavior**: Investigate the tribological behavior of PTFE composites filled with α-Al₂O₃ and SiO₂ nanoparticles when sliding against steel counterparts under different loads.
- **Friction Film Formation and Structural Evolution**: Study the formation of friction films and their structural evolution process in these composites under different loads.
- **Relationship Between Mechanical Strength and Tribological Applications**: Establish the connection and mechanism between maintaining mechanical strength and the tribological applications of polymer materials during service.
- **Scientific Data and Theoretical Guidance for Long-term Applications**: Provide corresponding scientific data and theoretical guidance for the long-term application of polymer lubricant materials.

3. **Research Objectives**:
- Reveal the impact of nanoparticle properties on the tribological behavior and friction film structure of mixed PTFE composites under different normal loads.
- Gain an in-depth understanding of the tribochemical reaction process of nanoparticles and their influence on friction film formation.

Through these studies, the paper aims to provide scientific basis and technical support for improving the tribological performance of PTFE composites and extending their service life.