Mechanochemical Effect of Filler Surface Functionality on Fluoropolymer Tribology

Wei Sun,Xiaojun Liu,Qingrui Song,Kun Liu,Wei Wang,Yunxiang Lu,Jiaxin Ye

DOI: https://doi.org/10.1021/acs.macromol.1c00395

IF: 5.5

2021-06-30

Macromolecules

Abstract:The 10 000× wear resistance improvement of PTFE by a trace amount of nanofillers has been heavily studied in the past decade and attributed to the moisture-dependent, mechanochemical formation of adherent and carboxylate salt-rich transfer films. However, debates still exist on the role of the fillers in wear reduction. Based on experimental and computational studies of selected PTFE nanocomposites, we proposed that (1) filler-driven polymer defluorination was the first and key step in the mechanochemistry; (2) effective wear-reducing fillers lowered the energy barrier of the defluorination; and (3) filler surface functionality, the amount of chelation products in transfer film, and wear resistance were strongly correlated. This hypothesis was further supported by thermal experiments in this study, which showed that the mechanochemistry and wear resistance were both thermally sensitive.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.macromol.1c00395?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.macromol.1c00395</a>.Details on the filler properties and composite mechanical properties used in this study (Table S1 and S2), XRD, TEM measurement results of fillers (Figure S1 and S2), illustration of the free-space length technique (Figure S3), nanoindentation measurement results for composites (Figure S4), schematic diagram of the tribological experiments (Figure S5), DFT-optimized structures for fluorocarbon absorbed on filler surface and calculated vibration vibrational forms of carboxylate salts (Figures S6 and S7), wear results of composites tested in the elevated temperatures (Figure S8) (<a class="ext-link" href="/doi/suppl/10.1021/acs.macromol.1c00395/suppl_file/ma1c00395_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

polymer science