Abstract:Aligned CNx (x < 0.1) nanotubes have been generated by pyrolyzing ferrocene/C-60 mixtures at 1050 degrees C in an ammonia atmosphere. The structure and composition of the product were determined by high-resolution transmission electron microscopy and high spatial resolution electron energy-loss spectroscopy. The CNx tubes (15-70 nm diameter, < 50 mu m length) grown in large flakes (< 3 mm(2)) consist of a reduced number of "graphitic" layers (< 15 on either side) arranged in a bamboo-like structure. Areas of high nitrogen concentration were found within curved or corrugated "graphite-like" domains. The observation of a well-developed double peak in the sigma* feature of the N K-edge suggests that the material has not undergone the transition to the fullerene-like phase known for nitrogenated carbons. Incorporation of nitrogen from the gas phase (NH3) into CNx nanotubes therefore leads to improved and more efficient N substitution into the network as compared to the synthesis with solid nitrogen-containing precursors reported earlier. (C) 2000 American Institute of Physics. [S0003-6951(00)04638-6].

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Large‐Scale Synthesis of Rings of Bundled Single‐Walled Carbon Nanotubes by Floating Chemical Vapor Deposition

Long Bundles of Aligned Carbon Nanofibers Obtained by Vertical Floating Catalyst Method

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Production of novel amorphous carbon nanostructures from ferrocene in low-temperature solution

Direct Synthesis of Long Single-Walled Carbon Nanotube Strands.

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Synthesis of Carbon Nanotube Bundles with Mesoporous Structure by a Self-Assembly Solvothermal Route

Synthesis of Thin-walled Carbon Nanotubes

Aligned array of N 2 -encapsulated multilevel branched carbon nanotubes

Formation of Close-Packed Multi-Wall Carbon Nanotube Bundles

A one-step single source route to carbon nanotubes

Aligned Cnx Nanotubes By Pyrolysis Of Ferrocene/C-60 Under Nh3 Atmosphere

Controllable preparation of triple-walled carbon nanotubes and their growth mechanism.

Preparation of Double-Walled Carbon Nanotubes

Encapsulated Nanowires Formed by Nanotube-Assisted Oriented Attachment

Preparation of novel carbon nanorods and nanotubes using poly(ferrocenylsilanes) as self-catalyzed precursors

Electronic Interactions and Polymer Effect in the Functionalization and Solvation of Carbon Nanotubes by Pyrene- and Ferrocene-Containing Poly(1-Alkyne)S

Preparation of highly pure double-walled carbon nanotubes

Production Of Large Area Carbon Nanotube Bundles On Metal Substrate

Preparation and Characterization of Bundled One-Dimensional Si3N4 Single-Crystalline Nanowires by Catalytic Pyrolysis of a Polymer Precursor