Abstract:Well-aligned carbon nitride nanotubes are fabricated by microwave plasma assisted chemical vapor deposition using iron as the catalyst. These nanotubes are linearly polymerized by carbon nitride nanobells with catalyst particles in the root, as revealed by high-resolution transmission electron microscopy. Carbon nitride nanotube film is analyzed by x-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and Raman spectroscopy. Both XPS and AES reveal a nitrogen content of about 2% in the film. Raman spectroscopy exhibits a good crystallization of these carbon nitride nanotubes. Electron energy loss spectroscopy is used to study the local distribution of nitrogen in a single nanotube, which indicates that nitrogen prefers to locate at curved graphite sheets, at the top of the nanobells, and that incorporation of nitrogen results in the decrease of the crystallization. Based on these results, a growth model is proposed to explain this periodically stacked nanobell structure. In this model, we propose that graphite sheets only precipitate along the surface of catalyst particles and that lower growth rate at the top curve surface of the bell-like catalyst particle is the key factor influencing formation of this special microstructure. A heterojunction between a tubular carbon nanotube and a carbon nitride nanobell also has been fabricated by a two-step growth technique. And short carbon nitride nanotubes with a few nanobells or even just one nanobell are obtained by both physical and chemical methods. Furthermore, we studied the field emission properties and have obtained a threshold field of as low as about 1 V/μm. A novel side-emission mechanism has been proposed based on the special polymerized nanobell structures.

Aligned array of N 2 -encapsulated multilevel branched carbon nanotubes

Synthesis of vertically aligned boron nitride nanotubes with a template of single-walled carbon nanotubes

Confined Growth of Carbon Nanotubes in Nanocutting Channel on Highly Oriented Pyrolytic Graphite

Aligned Cnx Nanotubes By Pyrolysis Of Ferrocene/C-60 Under Nh3 Atmosphere

Production of Aligned Carbon Nanotube Films and Nitrogen Doped Carbon Nanotube Films from the Pyrolysis of Styrene

Encapsulated Nanowires Formed by Nanotube-Assisted Oriented Attachment

Fe2O3 Particles Encapsulated Inside Aligned CNx Nanotubes

Synthesis and Microstructure of Fe3c Encapsulated Inside Chain-Like Carbon Nanocapsules

SYNTHESIS OF ALIGNED CARBON NANOTUBES ARRAY BY RADIO FREQUENCY PLASMA-ENHANCED HOT FILAMENT CHEMICAL VAPOR DEPOSITION

CVD Growth of N-Doped Carbon Nanotubes on Silicon Substrates and Its Mechanism

Layered Growth of Aligned Carbon Nanotubes Arrays on Silicon Wafers

Controlling Growth and Field Emission Property of Aligned Carbon Nanotubes on Porous Silicon Substrates

Doped Carbon Nanotube Array with a Gradient of Nitrogen Concentration

Long Bundles of Aligned Carbon Nanofibers Obtained by Vertical Floating Catalyst Method

The Fabrication And Characterization Of N-Doped Aligned Carbon Nanotube Arrays In Large Area

Polymerized Carbon Nitride Nanobells

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Template-confined growth and structural characterization of amorphous carbon nanotubes

Nitrogen-doped carbon nanotubes synthesized with carbon nanotubes as catalyst

Catalytic Growth Of Branching Carbon Nanotubes

Synthesis and Characterization of Well-Aligned Carbon Nitrogen Nanotubes by Microwave Plasma Chemical Vapor Deposition