Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Encapsulated Nanowires Formed by Nanotube-Assisted Oriented Attachment

One-dimensional Sub-stoichiometric W3O8Nanowires Filled Carbon Nanotubes

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Plumbing carbon nanotubes

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Encapsluation Of Co And Pd Multi-Metal Nanowires Inside Multiwalled Carbon Nanotubes By Microwave Plasma Chemical Vapor Deposition

A Novel Process from Cobalt Nanowire to Co3O4nanotube

Graphite-like Carbon-Encapsulated Iron Nanoparticle Self-Assembly into Macroscopic Microtube Structures

Assembly of non-crystalline cobalt particles into crystalline tricobalt tetroxide nanowires under an external magnetic field

Nanoscale Assembly of Nanowires Templated by Microtubules

Hydrogen Bubble-Directed Tubular Structure: A Novel Mechanism to Facilely Synthesize Nanotube Arrays with Controllable Wall Thickness

Compound growth and microstructure of carbon nanotube

Production and Characterization of Single-Crystal Feco Nanowires Inside Carbon Nanotubes

Au Nanowires Encapsulated in Carbon Nanotubes: Structure, Melting and Mechanical Properties

Filling Double-Walled Carbon Nanotubes with WO3 and W Nanowires Via Confined Chemical Reactions.

Super-long continuous Ni nanowires encapsulated in carbon nanotubesElectronic supplementary information (ESI) available: SEM images. See http://www.rsc.org/suppdata/cc/b4/b405444j/

Formation of multi-walled carbon nanotubes by catalytic chemical vapour deposition using zeolite encapsulated nanocrystalline cobalt oxides

Super-long continuous Ni nanowires encapsulated in carbon nanotubes.

Cobalt-catalysed growth of carbon nanotubes with single-atomic-layer walls

Growing pillars of densely packed carbon nanotubes on Ni-coated silica

Aligned array of N 2 -encapsulated multilevel branched carbon nanotubes