Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Preparation of Double-Walled Carbon Nanotubes

Synthesis of Double-Walled Carbon Nanotubes by Floating Chemical Vapor Deposition Method in a Reactor with Varied Diameter

Preparation of highly pure double-walled carbon nanotubes

Preparation of monodispersed multi-walled carbon nanotubes in chemical vapor deposition

Catalytic Growth of Multi-Wall Carbon Nanotubes on Carbon Cloth Using Powdery Ferrous Sulfate Heptahydrate As Catalyst Precursor

Controllable preparation and properties of single-/double-walled carbon nanotubes

Raman Characterization and Tunable Growth of Double-Wall Carbon Nanotubes

Large-Scale Synthesis of Long Double-Walled Carbon Nanotubes

Synthesis and Purification of Carbon Nanotubes

Novel Aerosol Method for Aligned Carbon Nanotubes Synthesis

Carbon Nanotube Synthesis and Parametric Study Using CaCO3 Nanocrystals As Catalyst Support by CVD

A Solid-state Hybrid Method to Synthesize Straight Carbon Nanotubes by Pyrolysis of Two Mixed Metal Phthalocyanines

Synthesis of multi-walled carbon nanotubes by microwave plasma-enhanced chemical vapor deposition

Controllable growth of double wall carbon nanotubes in a floating catalytic system

Synthesis and growth of multi-walled carbon nanotubes (MWNTs) by CCVD using Fe-supported zeolite templates

Precise control of the number of walls formed during carbon nanotube growth using chemical vapor deposition

Synthesis of Thin-walled Carbon Nanotubes

One-step Path to Highly Crystalline Multi-Walled Carbon Nanotubes with Large Inner Diameters

Effect of Temperature, Pressure, and Gas Ratio of Methane to Hydrogen on the Synthesis of Double-Walled Carbon Nanotubes by Chemical Vapour Deposition

Resonant Raman Scattering of Double Wall Carbon Nanotubes Prepared by Chemical Vapor Deposition Method