Abstract:The conventional synthesis of porous carbon materials is primarily relied on the activation and template process. This work successfully develops a one-step method for preparing amorphous porous carbon nanoparticles (APCNs) with a high specific surface area (SSA) in organic solvents under ambient atmosphere. The APCNs are formed mainly by the reaction of ferrocene with ammonium chloride at only 180 °C for 1 h in different solvents. Several ferrocene derivatives and KOH activation are also utilized to improve the textural properties of the APCNs. It is found that the high solubility of (C5H5)2Fe and FeCl3·6H2O in a solvent is the most essential factor associated with the decrease of carbon nanoparticle size. The smaller the nanoparticle size, the larger the SSA of APCNs. The APCNs prepared in phenoxyethanol have a median size of 32.74 nm, exhibiting an SSA of 689 m2/g. The high solubility of NH4Cl can also contribute to reducing the nanoparticle size. The binary solvent consisting of phenoxyethanol and glycol has an excellent solubility for (C5H5)2Fe, FeCl3·6H2O, and NH4Cl, in which the prepared APCNs have a median size 11.48 nm and a higher SSA of 936 m2/g. Besides, the benzoyl substituted group on the cyclopentadiene can facilitate formation of small mesopores. The oxygen and nitrogen are in situ doped in the APCNs. Activation is also effective, and the SSA of APCNs reaches a maximum value of 1575 m2/g at a KOH ratio of 2:1. The solvent-based synthesis is unique and competitive in terms of high efficiency and energy conservation.

Production of novel amorphous carbon nanostructures from ferrocene in low-temperature solution

Solvothermal Preparation of Amorphous Carbon Nanotubes and Fe/C Coaxial Nanocables from Sulfur, Ferrocene, and Benzene

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Synthesis and Characterizations of Amorphous Carbon Nanotubes by Pyrolysis of Ferrocene Confined Within Aam Templates

Long Bundles of Aligned Carbon Nanofibers Obtained by Vertical Floating Catalyst Method

Synthesis of Carbon/Carbon Core/Shell Nanofibers by Co-Pyrolysis of Tetrahydrofuran and Ferrocene

Preparation of novel carbon nanorods and nanotubes using poly(ferrocenylsilanes) as self-catalyzed precursors

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

One-step Path to Highly Crystalline Multi-Walled Carbon Nanotubes with Large Inner Diameters

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

The synthesis of carbon nanotubes at low temperature via carbon suboxide disproportionation

Aligned Cnx Nanotubes By Pyrolysis Of Ferrocene/C-60 Under Nh3 Atmosphere

A one-step single source route to carbon nanotubes

Synthesis of Carbon–fe3o4 Coaxial Nanofibres by Pyrolysis of Ferrocene in Supercritical Carbon Dioxide

Confined self-assembly approach to produce ultrathin carbon nanofibers.

Low-temperature organic solvent-based synthesis of amorphous porous carbon nanoparticles with high specific surface area at ambient atmosphere

A Novel Route To Multiwalled Carbon Nanotubes And Carbon Nanorods At Low Temperature

The Growth of New Extended Carbon Nanophases from Ferrocene Inside Single-Walled Carbon Nanotubes

Synthesis and Magnetic Properties of Fe3O4/helical Carbon Nanofiber Nanocomposites from the Catalytic Pyrolysis of Ferrocene

Controlled Synthesis and Phase Transformation of Ferrous Nanowires Inside Carbon Nanotubes