Abstract:Nanocrystalline Ni-Mo alloy coatings with excellent brightness, high hardness, and corrosion resistance were prepared. Nanocrystalline Ni-Mo alloy coating with a Mo content of 14.94 at% was electrodeposited on the copper foil substrate under the optimized conditions with the current efficiency of 51.64%. The electrodeposition behavior of Ni-Mo alloy coatings was studied by cathodic polarization curve and chronopotentiometry. Chronopotentiometry showed that the nucleation rate of Ni-Mo alloys can be accelerated with the increase of current density. Meanwhile, the cathodic polarization curves show that the additives can effectively inhibit the electrodeposition of Ni-Mo alloys. The (2 0 0) and (2 2 0) diffraction peaks of Ni gradually disappeared and the grain size gradually decreased with the increase of Mo content in the alloy coating according to XRD and TEM analysis. Scanning electron microscope (SEM) and confocal microscope observation results show that the coating becomes smoother and denser with the increase of Mo content when Mo content was lower than 14.94 at%, after which the density of the coating saw a decline due to the intensified hydrogen evolution reaction. The microhardness results of the alloy coating show that the microhardness of the alloy coating is related to the solid solution strengthening, texture evolution, and plastic deformation of the alloy. Meanwhile, the alloy coating has a Hall-Petch relationship and inverse Hall-Petch relationship, and the critical grain size is 5.5 nm. The corrosion resistance of Ni-Mo alloy coating is better than that of pure Ni coating, and the corrosion resistance is optimal when the Mo content is about 15 at%. In addition, in the plating solution containing additives, the deposited Ni-Mo alloy coating is smoother and denser, and the hardness and corrosion resistance of the alloy coating is also greatly improved.

The Effect Of Ph Value And Moo42- Concentration On The Plating Rate And Structure Of Electroless Ni-Mo-P Alloys

Effects of Ph Value and Concentration of Solution on P Content and Deposition Rate During Electroless Ni-P Plating on Aluminum Substrate Surface

Electrodeposition of nanocrystalline Ni-Mo alloys in pyrophosphate baths

Effect of pH Value on Ni-Cr-Mo Alloy Coating Prepared by Pulse Electroplating

Effects of Ligands on Electroless Ni–P Alloy Plating from Alkaline Citrate–ammonia Solution

Effect of Process Parameters on Electrodeposition Process of Co-Mo Alloy Coatings

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

A Study of Electroless Ni-Co-P Alloy Plating on Glass Fiber

A Study of Electroless Ni-Co-Fe-P Plating on Glass Fibers

Study of Electroless Ni-Zn-P Alloy Plating from Acidic Bath

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

Research on Amorphous Ni-Cu-P Alloy Plating

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

Preparation and Microstructure of Nanocrystalline Fe-Ni-Mo Alloy with Low Mo and High Fe Content

Effects of Surfactants in an Electroless Nickel-Plating Bath on the Properties of Ni−P Alloy Deposits

Preparation of Amorphous-Nanocrystalline Composite Structured Ni–P Electrodeposits

Effect of Process Parameters on Deposition Rate of Electroless Ni-P Plating on AZ91D Magnesium Alloy

Stress And Corrosion Performance Of Amorphous Ni-Mo-P Electroless Deposits

Effect of Adding Modes of Plating Solution on Low Phosphorous Electroless Nickel Plating

Electroplating of Ni_(70)Cu_(30) alloy from pyrophosphate bath

Effect of Pickling Processes on the Microstructure and Properties of Electroless Ni–P Coating on Mg–7.5Li–2Zn–1Y Alloy