Bulk Dense Fine-Grain (1−x)bisco3–xpbtio3 Ceramics with High Piezoelectric Coefficient

Tingting Zou,Xiaohui Wang,Han Wang,Caifu Zhong,Longtu Li,I-Wei Chen

DOI: https://doi.org/10.1063/1.2995861

IF: 4

2008-01-01

Applied Physics Letters

Abstract:High density fine grain (1−x)BiScO3–xPbTiO3 ceramics were successfully prepared by two-step sintering and their ferroelectric properties were investigated. Experimental evidence indicates the existence of a morphotropic phase boundary at the composition x=0.635, which exhibits a piezoelectric coefficient d33 of 700 pC/N at room temperature, significantly higher than the reported values to date. Furthermore, a higher electromechanical coupling factor Kp=0.632 and a larger remnant polarization Pr=47.3 μC/cm2 were obtained. The paraelectric-to-ferroelectric phase transition occurs at 446 °C, slightly lower than in the coarse grain ceramics with a similar composition, suggesting a grain size effect. The local effective piezoelectric coefficient d33∗ was estimated to be 795 pC/N at 2.29 V, measured by scanning probe microscopy. Further atomic force microscope observation revealed the existence of 90° domains of about 60–70 nm in width, confirming the previous results that small domain structure enhances the piezoelectric properties.