High Piezoelectric D33 Coefficient in (ba1−xcax)(ti0.98zr0.02)o3 Lead-Free Ceramics with Relative High Curie Temperature

Wei Li,Zhijun Xu,Ruiqing Chu,Peng Fu,Guozhong Zang

DOI: https://doi.org/10.1016/j.matlet.2010.07.042

IF: 3

2010-01-01

Materials Letters

Abstract:Lead-free (Ba1−xCax)(Ti0.98Zr0.02)O3 (x=0–0.04) ceramics were prepared successfully using a solid-state reaction technique. The polymorphic phase transitions (PPT) from orthorhombic to tetragonal phase around room temperature were identified in the composition range of 0<x<0.03. High piezoelectric coefficient of d33=375pC/N and planar electromechanical coupling factor of kp=44.1% were obtained for the samples at x=0.01. With the increase of Ca content, the orthorhombic–tetragonal phase transitions shifted towards room temperature, while relative high Curie temperature (TC) was still maintained about 115°C.