Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Preparation And Characterization Of Activated Carbons From Biomass-Based Carbon Through Phosphoric Acid Activation

Preparation of Phosphate-activated Carbon from the Coconut Fibers

Biomass-Based Activated Carbon and Activators: Preparation of Activated Carbon from Corncob by Chemical Activation with Biomass Pyrolysis Liquids

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Preparation of Activated Carbon from Co-Pyrolysis Activation of Fly Ash and Biomass

Preparation and Electrochemical Properties of PF-based Activated Carbon

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

Preparation,Characterization and Absorption Capability of Activated Carbon from Anaerobic Digested Residue of S.alterniflora

Effect of Two-Stage Process on the Preparation and Characterization of Porous Carbon Composite from Rice Husk by Phosphoric Acid Activation

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Comparative Study on the Performance and Mechanism of Adsorption–Oriented Phosphorus–Modified High–Efficiency and Durable Activated Biochar from Fast Pyrolysis

Preparation of activated carbon through the pyrolysis of waste bamboo chips and evaluation of its CO2 adsorption efficacy

Preparation of Activated Carbon from the Residual Carbon Obtained by Fast Pyrolysis of Biomass

PREPARATION OF ACTIVATED CARBON FROM S.ALTERNIFLORA BY H_3PO_4 CHEMICAL ACTIVATION

Physical and chemical properties of carbons synthesized from xylan, cellulose, and Kraft lignin by H3PO4 activation

Preparation of porous carbons from non-metallic fractions of waste printed circuit boards by chemical and physical activation

Study on the preparation of high value-added activated carbon from petroleum coke: Comparison between one- and two-step methods for carbonization and activation

Optimized preparation of multi-matrix activated carbon for CO 2 capture by response surface methodology: The advantages of co-pyrolysis of biomass and plastics

Physicochemical Properties of Carbons Prepared from Pecan Shell by Phosphoric Acid Activation

Enhanced Abundance of Oxygen-Containing Intermediates from Pre-Oxidation of Poplar Sawdust Facilitates Generation of Porous Structures in Activation with Phosphoric Acid