Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

PREPARATION OF ACTIVATED CARBON FROM S.ALTERNIFLORA BY H_3PO_4 CHEMICAL ACTIVATION

Preparation,Characterization and Absorption Capability of Activated Carbon from Anaerobic Digested Residue of S.alterniflora

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Preparation and pore characterization of activated carbon from Ma bamboo (Dendrocalamus latiflorus) by H3PO4 chemical activation

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

Physical and chemical properties of carbons synthesized from xylan, cellulose, and Kraft lignin by H3PO4 activation

Carbons Prepared from Spartina Alterniflora and Its Anaerobically Digested Residue by H3PO4 Activation: Characterization and Adsorption of Cadmium from Aqueous Solutions.

Surface Chemistry of Cherry Stone-Derived Activated Carbon Prepared by H3PO4 Activation

Preparation and Electrochemical Properties of PF-based Activated Carbon

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Methods for preparation and activation of activated carbon: a review

Preparation, characterization and adsorption performance of mesoporous activated carbon with acidic groups

Optimization of Preparation of Microporous Activated Carbon with High Surface Area from Spartina Alterniflora and Its P-Nitroaniline Adsorption Characteristics

Preparation of green alga-based activated carbon with lower impregnation ratio and less activation time by potassium tartrate for adsorption of chloramphenicol

PREPARATION OF ACTIVATED CARBON FROM (PISTACIA KHINJUK PEELS) AND STUDY ITS CHEMICAL PROPERTIES

ADSORPTION OF CADMIUM FROM AQUEOUS SOLUTIONS ON ACTIVATED CARBON PREPARED FROM S.ALTERNIFLORA

Effect of Co-solution of Carbon Precursor and Activating Agent on the Textural Properties of Highly Porous Activated Carbon Obtained by Chemical Activation of Lignin With H3PO4

Adsorption of lead ions onto activated carbon prepared from bio-plant stems activation with H_3PO_4

The Influence of NH4NO3 and NH4ClO4 on Porous Structure Development of Activated Carbons Produced from Furfuryl Alcohol

Preparation of Activated Carbon from Co-Pyrolysis Activation of Fly Ash and Biomass