Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Yanping Guo,David A. Rockstraw

DOI: https://doi.org/10.1016/j.micromeso.2006.10.006

IF: 5.876

2006-01-01

Microporous and Mesoporous Materials

Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.