Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Macroporous Activated Carbon Fibers from Rayon Precursors Impregnated with Phosphoric Acid

Adsorption of Volatile Organic Compounds on Activated Carbon Fiber Prepared by Carbon Dioxide

Preparation of activated carbon fabrics from cotton fabric precursor

Fabrication and Evaluation of Mesoporous Poly(vinyl Alcohol)-Based Activated Carbon Fibers

PVA-based Activated Carbon Fibers with Lotus Root-Like Axially Porous Structure

Preparation and hydrogen storage of activated rayon-based carbon fibers with high specific surface area

Preparation and pore characterization of activated carbon from Ma bamboo (Dendrocalamus latiflorus) by H3PO4 chemical activation

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Physical and chemical properties of carbons synthesized from xylan, cellulose, and Kraft lignin by H3PO4 activation

Structure Evolution and Optimization in the Fabrication of Pva-Based Activated Carbon Fibers

Preparation of pitch-based activated carbon fibers with high specific surface area and excellent adsorption properties

Activated Carbon Powders from Wool Fibers

Porous carbon fibers from low-temperature sodium amide activation for acetone adsorption

Preparation and Characterization of Activated Carbon Fiber (ACF) from Cotton Woven Waste

Phosphorous - Containing Activated Carbon Derived From Natural Honeydew Peel Powers Aqueous Supercapacitors

Effect of beating degree of fiber on the development of porosity in polyacrylonitrile-based activated carbon fiber paper

Preparation and Properties of Phenolic Resin-Based Activated Carbon Spheres with Controlled Pore Size Distribution

Structural Evolution of Polyimide-Derived Carbon during Phosphoric Acid Activation

Efficient dye adsorption of mesoporous activated carbon from bamboo parenchyma cells by phosphoric acid activation

Effects of the heating history of impregnated lignocellulosic material on pore development during phosphoric acid activation

Versatile Activated Carbon Fibers Derived from the Cotton Fibers Used as CO2 Solid-State Adsorbents and Electrode Materials