Abstract:Activated carbons were prepared from rice hull by one-step phosphoric acid activation in this work. The evolution of pore structure and surface chemistry in the activation temperature range of 170–450°C was investigated through various characterization techniques. The results showed that the development of porosity (extent of activation) was negligible at activation temperature below 300°C, and rapid evolution occurred in 300–400°C. Porous activated carbon with bimodel pore structure (pore<1nm and pore>1nm) and BET surface area as high as 1295m2/g was obtained at 450°C. The ash contents of samples prepared in this study were in the range of 5–21%. The ash contents of carbons prepared in this study initially decreased from 21.03% to 4.89% with the change of temperature from 170 to 300°C, then increased to 8.72% at 450°C. Boehm titration results suggested that low activation temperature (⩽300°C) benefits the formation of acidic surface groups. With the increase of activation temperature from 300 to 350°C, the concentrations of strong, intermediate and weak acidic surface groups decreased from 2.23, 1.87, and 2.73 to 1.66, 1.32, and 2.16mmolH+/g, respectively. Over 350°C, the change of these groups were insignificant. FTIR results revealed the existence of carbonyl-containing, phosphorus-containing groups, and groups containing Si–O bond. The relative concentration of carbonyl-containing groups decreases with an increase in activation temperature, while that of phosphorus-containing groups follows the reverse trend. The content of Si–O decreased first, then slowly increased with the increase of activation temperature. Boehm titration and FTIR (Fourier transform infrared spectroscopy) results indicated that the surfaces of these carbons contain both temperature-sensitive and temperature-insensitive groups. The temperature-sensitive part consists mainly of carbonyl-containing groups, such as carboxylic groups, while the temperature-insensitive part is primarily phosphorus-containing groups and groups containing Si–O bond. This study demonstrated that carbon products with relative low ash content and high activation degree can be prepared from rice hull by H3PO4 activation at suitable temperature.

Change of Morphology of Rice Derived Spherical Hydrochar During Activation

Bamboo Derived Hydrochar Microspheres Fabricated by Acid-Assisted Hydrothermal Carbonization.

Activation of mixed sawdust and spirulina with or without a pre‐carbonization step: Probing roles of volatile-char interaction on evolution of pyrolytic products

Activation of Pine Needles with Zinc Chloride: Evolution of Functionalities and Structures of Activated Carbon Versus Increasing Temperature

Activated Carbons Prepared from Rice Hull by One-Step Phosphoric Acid Activation

Activation of Poplar Sawdust and Anthracite Coal: Distinct Involvement of Aliphatic and Aromatic Structures in Pore Development

Dye Removal of Activated Carbons Prepared from NaOH-pretreated Rice Husks by Low-Temperature Solution-Processed Carbonization and H3PO4 Activation

KOH Activation Mechanism in the Preparation of Brewer's Spent Grain-Based Activated Carbons

Thermal pretreatment of willow branches impacts yield and pore development of activated carbon in subsequent activation with ZnCl2 via modifying cellulose structure

Syngenetic Effects in Co-Activation of Willow Wood with Homogenous Biochar Facilitate Pore Generation in Activation

Adsorption Characterization and Activation Behavior of Biomass Chars Produced by Hydrothermal Carbonization

Evaluating Performance of Pyrolysis and Gasification Processes of Agriculture Residues-Derived Hydrochar: Effect of Hydrothermal Carbonization

Impacts of partial removal of lignin on development of pore structures in activation of Chinese parasol

Enhancing biochar production: A technical analysis of the combined influence of chemical activation (KOH and NaOH) and pyrolysis atmospheres (N 2 /CO 2 ) on yields and properties of rice husk-derived biochar

Enhanced Abundance of Oxygen-Containing Intermediates from Pre-Oxidation of Poplar Sawdust Facilitates Generation of Porous Structures in Activation with Phosphoric Acid

Enhancing biochar production: A technical analysis of the combined influence of chemical activation (KOH and NaOH) and pyrolysis atmospheres (N2/CO2) on yields and properties of rice husk-derived biochar

Preparation of Corn Straw-Based Carbon by “Carbonization-Koh Activation” Two-Step Method: Gas–solid Product Characteristics, Activation Mechanism and Hydrogen Storage Potential

Preparation of Activated Carbon from Pyrolyzed Rice Husk by Leaching out Ash Content after CO2 Activation

Effects of Alkali/Char Ratio and Activation Temperature on Ultramicropores of Rice Husk Active Carbon

Physical and chemical properties of carbons synthesized from xylan, cellulose, and Kraft lignin by H3PO4 activation

Mechanism of Biomass Activation and Ammonia Modification for Nitrogen-Doped Porous Carbon Materials.