A simple and highly effective process for the preparation of activated carbons with high surface area
Ying Li,Xuefeng Ding,Yupeng Guo,Lili Wang,Chunguang Rong,Yuning Qu,Xiaoyu Ma,Zichen Wang
DOI: https://doi.org/10.1016/j.matchemphys.2011.02.046
IF: 4.778
2011-01-01
Materials Chemistry and Physics
Abstract:Activated carbons with high surface area were prepared by phosphoric acid as activation agent and rice husks as precursors. It was found that the characteristics of the activated carbons were influenced not only by the preparation but also by the post-processing method. The high surface area of the activated carbons was prepared under the optimum condition (50% H 3 PO 4 with impregnation ratio of 5:1, activation temperature of 500 °C, activation time of 0.5 h, wash water temperature of 100 °C). SiO 2 content could affect the surface area of activated carbons, either. The lower SiO 2 content of the activated carbons, the higher pore volume the carbons had. The SiO 2 content was 11.2% when used the optimum condition. The explanation was that silicon element in rice husks reacted with H 3 PO 4 to form silicon phosphate (SiP 2 O 7 ), and it could be proved further by X-ray diffraction analysis, SiP 2 O 7 could be removed by post-process. Keywords Activated carbon Rice husk Phosphoric acid Silicon phosphate 1 Introduction Activated carbons are of interest due to their extensive surface area, high degree of surface reactivity, and favorable pore size distribution [1] . Among the various activation agents, phosphoric acid is a well-established agent for preparation of activated carbons, which has many advantages. Nowadays, the raw material of phosphoric acid activation, usually stone [2–6] , shell [7,8] , polymer [9] , wood [10–12] and coal [11,13] , is limitative or expensive, or nonrenewable, which restrict their application. Thus lignocellulosic agricultural wastes are investigated as precursors due to their renewability and huge amount. Rice husk, a by-product of the rice milling industry, with an annual output 40 million tons in China [14,15] , usually burned in open heaps as waste, can be used as the precursor of the activated carbon. However, due to the high ash content of rice husk, which is difficult to remove, activated carbon prepared from rice husk by H 3 PO 4 activation with desirable surface area and pore volume often contains two procedures: alkali-leaching process to remove SiO 2 followed by H 3 PO 4 activation, surface area and pore volume reach 1741 m 2 g −1 and 1.315 ml g −1 [16] . In this work, we prepared activated carbons with high surface area (1820 m 2 g −1 ) using rice husks as raw materials by H 3 PO 4 activation without alkali-leaching process. The mechanism of phosphoric acid activation was enriched through this research. The characteristics of the activated carbon were greatly influenced by post-processing method. To our best knowledge, the carbons washed by water with different temperatures had different surface area, pore volume and ash content, which was first discussed in our manuscript. The whole process was simple and economical, which not only enlarge the scope of the raw materials through H 3 PO 4 activation, but also make it possible to produce high surface area activated carbons in industry. 2 Experimental 2.1 Precursors Rice husk is obtained from a rice mill nearby Changchun city. Rice husk was washed thoroughly with distilled water to remove soil and dust, then dried at 100 °C overnight and porphyrized to 60 mesh before employment. 2.2 Preparation of activated carbons The precursors were impregnated with phosphoric acid solution (40–85 wt.%) with impregnation ratio of (the weight ratio of phosphoric acid to rice husk) 3:1–6:1, and stirred for at least 2 min at room temperature, then the mixtures were heated up to different temperatures: 300, 400, 500, 600 °C for 0.5–2 h. The products were washed with hot distilled water (100 °C) for several times until the filtrate was neutral, then dried at 120 °C for 12 h before further characterization. 2.3 Characterization 2.3.1 Nitrogen adsorption Pore structure analysis was performed using a Micromeritics ASAP 2010 Surface Analyzer through nitrogen adsorption at 77 K in the relative pressure range of 10 −6 –1 atm. Prior to the analysis, all the samples were degassed at 200 °C to 3 μm Hg under vacuum. Surface area was calculated by the Brunauer, Emmett, and Teller (BET) equation using the data obtained from nitrogen adsorption isotherm. The relative pressure range used for the calculation was 0.05–0.2. The single point total pore volume was obtained from the amount of nitrogen adsorbed at a relative pressure around 0.95. The pore size distribution was derived from the adsorption branches of the isotherms by the Density Functional Theory (DFT) method. 2.3.2 X-ray diffraction The crystal structures of samples were characterized by X-ray diffraction (XRD) (SHIMADZU XRD-6000 diffractometer employing Ni-filtered Cu Kα radiation, at a scanning rate of 6° min −1 with 2 θ ranging from 15° to 60°). 2.3.3 Transmission electron microscopy (TEM) The surface morphology of the as-prepared samples was examined by transmission electron microscope (JEOL 2000EX) operating at 200 kV and high-resolution transmission electron micrograph (HRTEM FEI TECNAI G2). HRTEM equipped with an energy dispersive X-ray (EDX) analyzer (Phoenix). 3 Results and discussion 3.1 Characteristics of activated carbons Fig. 1 shows the TEM and HRTEM images of the activated carbons. It can be clearly conformed the nature of the amorphous structure from Fig. 1 a. The structure of the activated carbon was turbostratic with a pore structure consisting of inter-connected nanochannels, which were formed by the disordered packing of turbostratic carbon sheets and clusters [17] . Most pore size is smaller than 1 nm from HRTEM image ( Fig. 1 b). According to the IUPAC (International Union of Pure and Applied Chemistry) classification, the isotherms in this work were classified into type IV, H4. Fig. 2 shows adsorption/desorption isotherms of nitrogen at 77 K of activated carbons. It illustrates that the existence of microporous structure where pore filling occurs at low relative pressures. The presence of adsorption hysteresis loop indicates the presence of mesoporosity according to type IV, and the porous carbon contains slit-shaped pores according to H4. In this work, 2 and 50 nm were taken as the boundary sizes between micro and mesopore, and meso and macropore, respectively. From Fig. 3 , we can see that the pore diameter of the prepared activated carbon contain 1.3–2.4 nm, 2.7–4.5 nm, 6.8 nm and 9.7–11.0 nm, respectively, which indicates the porous carbon have micro and mesopore structure. 3.2 Effect of different factors on activated carbons 3.2.1 Influence of activation temperature The BET surface areas and pore volumes of activated carbons prepared at different activation temperatures using the impregnation ratio of 4:1, activation time of 1.5 h are summarized in Fig. 4 a and b . The concentration of H 3 PO 4 was 50, 60 and 85%, respectively. As seen in Fig. 4 a and b, the BET surface areas and pore volumes of activated carbons increase gradually with activation temperature increasing from 300 to 500 °C, then decrease with further increasing in the final activation temperature. With activation temperature of 300 °C, the activation extent of rice husk was relatively low demonstrated by the small surface area. With increasing temperature to 600 °C, violent gasification reactions might cause part of the pore structure to be destroyed by collapsing which caused the small surface area [18] . From Fig. 5 we can see the pore volume declined when the temperature increased to 600 °C, which could be deduced from the collapsing of pores. So the optimum temperature for activation was 500 °C. The ash content is shown in Fig. 4 c and Table 1 . The yield of activated carbon was calculated based on the weight of rice husk on a dry basis from the following equation: Yield of activated carbon ( wt . % ) = Weight of activated carbon Weight of rice husk Ash content of rice husk was around 18%, the yield of activated carbons was about 40%, so the ash content of activated carbons should be around 32% theoretically, but it decreased when the activation temperature was 400 or 500 °C, which could be explained that silicon element existed in rice husk reacted with H 3 PO 4 to form phosphate in this temperature range, and most of the phosphate could be removed by post-processing. However, as the temperature increased to 600 °C, the ash content of activated carbon became higher, which was due to the decreasing of the product yield. Fig. 6 shows the XRD patterns of activated carbons. As seen in Fig. 6 , all diffraction peaks are similar to those of silicon phosphate (SiP 2 O 7 ) and the diffraction data is in good agreement with JCPDS file no. 22-1320. As seen from Fig. 7 , the EDX shows the activated carbons have the element of C, Si, P, O, which prove further the existence of silicon phosphate in activated carbons. 3.2.2 Influence of activation time Fig. 8 a and b shows the BET surface areas and pore volumes of activated carbons prepared at different activation times with other factors are fixed at 500 °C, impregnation ratio of 4:1. The concentration of H 3 PO 4 was 50, 60 and 85%, respectively. As observed from Fig. 8 , the BET surface area and pore volume of activated carbon reach maximum value when the activation time is 0.5 h. The ash content of activated carbons increased with the increase of activation time, which was due to the soluble silicon compound may convert to other format that could deposit into the pores of activated carbons. It blocked the pores and resulted in the surface area decreasing and ash content increasing. From Fig. 9 we can deduce that when the duration time extending to 1.5 h, the pore diameter of 6.5–7.0 nm and 10–12 nm decreased rapidly. For the activated carbon prepared at 500 °C, 50% H 3 PO 4 impregnation ratio of 4:1, reaction time of 0.5 h, the BET surface area and pore volume reached 1712 m 2 g −1 and 1.968 ml g −1 , the ash content was 11.7%. 3.2.3 Influence of the concentration of H 3 PO 4 and impregnation ratio The effect of the different concentration of H 3 PO 4 on the surface area and pore volume of activated carbon were investigated at impregnation of 4:1 and reaction temperature of 500 °C. 40% H 3 PO 4 was also used as the activation agent, but the characteristics of the activated carbons were worse than 50% H 3 PO 4 as the activation agent. 50% H 3 PO 4 was better than others with the activation time of 0.5 h. When used 85% H 3 PO 4 , pore volume was larger and the surface area was smaller than the activated carbons produced by 50% H 3 PO 4 . The reaction was rigorous when using 85% H 3 PO 4 , caused some of the pores combining together and produced poor pore size distribution, therefore, the pore volume was large. The reaction was relatively moderate when using 50% H 3 PO 4 , resulting in narrow micropore size distribution and high surface area. The carbons with the highest surface area were obtained when the raw materials were impregnated with 50% H 3 PO 4 and then activated at 500 °C for 0.5 h, different impregnation ratios were used to find the optimum condition with other parameters constant. As seen from Fig. 10 , the optimal impregnation ratio for activation agent: rice husk is 5:1 (g/g). The BET surface area was 1820 m 2 g −1 , pore volume was 2.01 ml g −1 and ash content was 11.2%. Excessive impregnation was detrimental to activation, which was because H 3 PO 4 as flame retardant prevented the porosity development. Moreover, the excess of H 3 PO 4 and phosphates blocked the pores of the activated carbons. 3.2.4 Influence of the post-processing temperature The post-processing temperature had great influence on the characteristic of the activated carbon. The carbons (prepared at 500 °C, 50% H 3 PO 4 impregnation ratio of 5:1, reaction time of 0.5 h) washed by the water with different temperature had different surface area, pore volume and ash content. As seen in Table 2 , the ash content is high when the wash water is below 40 °C. As this study showed before that the silicon element could react with H 3 PO 4 to form SiP 2 O 7 . SiP 2 O 7 had a good solubility in hot water, but could not dissolve in cold water. If it could not be removed it deposited onto the carbons again, resulted in the low surface area and pore volume. Thus, the activated carbons characteristics were greatly improved by changing the post-processing temperature. 4 Conclusions This study had shown that rice husk could be used as raw material for preparation of activated carbons with high surface area and uniform pore size. The activated carbons contained micropores and mesopores. The pore diameter of the prepared activated carbon contain 1.3–2.4 nm, 2.7–4.5 nm, 6.8 nm and 9.7–11.0 nm, respectively. The ash content decreased when the optimum condition was used to prepare activated carbons. It could be deduced that silicon element in rice husks reacted with H 3 PO 4 to form silicon phosphate (SiP 2 O 7 ), and proved further the existence of SiP 2 O 7 in activated carbons by XRD analysis, SiP 2 O 7 had a good solubility in hot water, but was difficult to dissolve in cold water. Activated carbons with different surface areas and pore volumes were obtained when we changed reaction factors such as activation temperature, activation time and impregnation ratio. The post-processing temperature had a great influence on the characteristics of the activated carbons. These results provided us with a good method for preparation of activated carbon with rice husk and gave us a further understanding of the formation mechanism of carbon materials. This method could be extended to variety of materials such as rice bran and other husk shells. Acknowledgements This research was supported by the financial support of the China National Key Technology R&D Programme under Contract no. 2008BAE66B00 and Jilin Provincial Environmental Protection Department under Contract no. 200917 . References [1] Y. Guo D.A. Rockstraw Carbon 44 2006 1464 1475 [2] A.M. Puziy O.I. Poddubnaya R.P. Socha J. Gurgul M. Wisniewski Carbon 46 2008 2113 2123 [3] A.M. Puziy O.I. Poddubnaya A. Martínez-Alonso A. Castro-Muñiz F. Suárez-García J.M.D. Tascón Carbon 45 2007 1941 1950 [4] M. Molina-Sabio F. Caturla F. Rodríguez-Reinoso Carbon 33 1995 1180 1182 [5] M. Soleimani T. Kaghazchi Bioresour. Technol. 13 2008 5374 5383 [6] M. Molina-Sabio F. Rodríguez-Reinoso F. Caturla M.J. Sellés Carbon 33 1995 1105 1113 [7] A. Ahmadpour D.D. Do Carbon 35 1997 1723 1732 [8] W.C. Lim C. Srinivasakannan N. Balasubramanian J. Anal. Appl. Pyrolysis 2 2010 181 186 [9] A.M. Puziy O.I. Poddubnaya A. Martínez-Alonso F. Suárez-García J.M.D. Tascón Carbon 40 2002 1493 1505 [10] M. Jagtoyen F. Derbyshire Carbon 36 1998 1085 1097 [11] W.H. Lee P.J. Reucroft Carbon 37 1999 15 20 [12] P. Patnukao P. Pavasant Bioresour. Technol. 99 2008 8540 8543 [13] H. Teng T. Yeh L. Hsu Carbon 36 1998 1387 1395 [14] T. Li T. Wang Mater. Chem. Phys. 112 2008 398 401 [15] H. Zhang X. Zhao X. Ding H. Lei X. Chen D. An Bioresour. Technol. 101 2010 1263 1267 [16] T.H. Liou S.J. Wu J. Hazard. Mater. 171 2009 693 703 [17] T. Wang S. Tan C. Liang Carbon 47 2009 1880 1883 [18] H.O. Gyu R.P. Chong Fuel 81 2002 327 336