Abstract:Ultralong, single-crystal Ni2Si nanowires sheathed with amorphous silicon oxide were synthesized on a large scale by a chemical vapor transport (CVT) method, using iodine as the transport reagent and Ni2Si powder as the source material. Structural characterization using powder X-ray diffraction, electron microscopy, and energy-dispersive spectroscopy shows that the nanowires have Ni2Si-SiOx core-shell structure with single-crystal Ni2Si core and amorphous silicon oxide shell. The oxide shell is electrically insulating and can be removed by HF etching. Four-terminal electrical measurements show that the single-crystal nanowire has extremely low resistivity of 21 mu Omega center dot cm and is capable of supporting remarkably high failure current density > 10(8) A/cm(2). These unique Ni2Si nanowires are very attractive nanoscale building blocks for interconnects and fully silicided (FUSI) gate applications in nanoelectronics.

A Co-Reduction-Silicification Route To Delta-Ni2si Nanowire

A Co-reduction–Silicification Route to δ-Ni2Si Nanowire

Ultrafast growth of single-crystalline Si nanowires

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Phase-controlled Synthesis of Nickel Silicide Nanostructures

Tiny SiO2 nano-wires synthesized on Si (1 1 1 ) wafer

Sulfide-assisted Growth of Silicon Nano-Wires by Thermal Evaporation of Sulfur Powders

Silicon Nano-Wires Fabricated by a Novel Thermal Evaporation of Zinc Sulfide

Synthesis and Characterization of SiC Nanowires Through a Reduction−Carburization Route

Controlling the growth and field emission properties of silicide nanowire arrays by direct silicification of Ni foil.

Tiny silicon nano-wires synthesis on silicon wafers

Preparation of Nisi2 Nanowires with Low Resistivity by Reaction Between Ni Coating and Silicon Nanowires

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

A simple method to synthesize Si3N4 and SiO2 nanowires from Si or Si/SiO2 mixture

Growth of SiC Nanowires from NiSi Solution

Ultra‐Long Single‐Crystalline Α‐si3n4nanowires: Derived from a Polymeric Precursor

Synthesis of Nio Nanowires by an Oxidation Route

Synthesis of Si 3 N 4 Nanowires by Catalyst‐free Nitridation of (si + SiO 2 ) Mixture

Synthesis and Characterization of a Large Amount of Branched Ni 2 Si Nanowires

Nitridation of Silica to an Α‐silicon Nitride Nanorod Using NaNH2 in the Autoclave at 700°C

Ultralong Single-Crystal Metallic Ni<sub>2</sub>Si Nanowires with Low Resistivity