Abstract:In this work, millimeter-scale Si3N4@SiOx core-shell structure nanowires were synthesized using the direct nitridation method without the use of catalysts. The silicon powders used as raw materials were pretreated at 1300 degrees C for 3 h under ammonia. The ammonia was then converted into a nitrogen/hydrogen gas mixture and heated at 1350 degrees C for another 5 h. The morphology and structure of the as-obtained nanowires were investigated in detail. The Si3N4@SiOx nanowires with a core-shell structure were composed of a crystalline alpha-Si3N4 core and an amorphous SiOx shell. The formation of the alpha-Si3N4 core nanowire is due to the reaction of the N-2 gas with the byproduct SiO gas. However, the formation of the amorphous SiOx shell is related to the deposition location of the samples. For the inner part of the samples, the SiOx shell derives from the deposition of the byproduct SiO gas at 1350 degrees C, while the SiOx shell of the external part of the samples likely derives from the oxidation of the silicon nitride core during the cooling process.

Nitridation of Silica to an Α‐silicon Nitride Nanorod Using NaNH2 in the Autoclave at 700°C

Sulfur-assisted Fabrication of Silicon Nitride Nanorods in Autoclaves at 250 °C

Synthesis and Characterization of Α-Phase Silicon Nitride Powders by Direct Nitridation

Thermal Nitridation Kinetics of Silicon Wafers in Nitrogen Atmosphere During Annealing

Additive‐Assisted Nitridation to Synthesize Si3N4 Nanomaterials at a Low Temperature

Additive-Assisted Nitridation to Synthesize Si<sub>3</sub>N<sub>4</sub>Nanomaterials at a Low Temperature

Chemical Synthesis of Aluminum Nitride Nanorods in an Autoclave at 200 °C

Preparation Of Si3n4 Nanorods From Borosilicate Glass

Solid State Synthesis of Nitride, Carbide and Boride Nanocrystals in an Autoclave

Synthesis of Α Silicon Nitride Single-Crystalline Nanowires by Nitriding Cryomilled Nanocrystalline Silicon Powder

Mass Production of Α-Silicon Nitride Single-crystalline Nanowires

Co-Catalyzed Nitridation Of Silicon And In-Situ Growth Of Alpha-Si3n4 Nanorods

Direct Synthesis of Α-Silicon Nitride Nanowires from Silicon Monoxide on Alumina

Synthesis of Sub-micron Spherical Α-Si3n4 Powder by Direct Nitridation of Silicon Saw Dust

Sulfur-assisted synthesis of nitride nanocrystals.

Large Scale Synthesis of Si3N4@SiOx Core-Shell Structure Nanowires by Direct Nitridation

Growth Of Sic Nanorods At Low Temperature

Liquid-Phase-Assisted Catalytic Nitridation of Silicon and In Situ Growth of α-Si3N4

Nitridation Of Silicon With Ammonia And Nitrogen

Synthesis and Characterization of Amorphous Silicon Nitride Nanoparticals and α‐Silicon Nitride Nanowires

Needle-Like SiC Nanorods