Abstract:At present, the carbothermal reduction and nitridation process is an important method for the large-scale preparation of aluminum nitride powder in industry, but the tremendous energy consumption caused by long-term high temperatures seriously restricts its practical application. To solve this problem, the (NaAlO2+C) mixture with a mole ratio of NaAlO2:C = 1:3 was prepared based on sodium aluminate and carbon black which has been ball milled with anhydrous ethanol as a grinding liquid. The crystal structure evolution and nitridation reaction behavior of sodium aluminate at 800–1600 °C under a nitrogen atmosphere in the presence of carbon were systematically studied employing XRD, SEM, and ICP-MS. The results showed that: high energy θ-Al2O3, η-Al2O3 can be excited by heating sodium aluminate to 1400 °C under a nitrogen atmosphere in the presence of carbon. The transformation process between sodium aluminate and aluminum nitride is carried out via the direct nitridation of θ-Al2O3, η-Al2O3. Benefiting from the direct nitridation of η-Al2O3 and θ-Al2O3, high-purity aluminum nitride powder with a particle size of 0.50 ± 0.18 μm was synthesized at 1400 °C. This work provides a new path for reduced energy consumption in the aluminum nitride industry.

Chemical Synthesis of Aluminum Nitride Nanorods in an Autoclave at 200 °C

Synthesis and optical properties of hexagonal aluminum nitride nanocrystals

Nitridation of Silica to an Α‐silicon Nitride Nanorod Using NaNH2 in the Autoclave at 700°C

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

The Growth Mechanism of Monocrystal Aluminum Nitride Nanowires at Low Temperature

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Synthesis of Nanocrystalline Aluminum Nitride by Nitridation of Δ‐al2o3 Nanoparticles in Flowing Ammonia

Synthesis of Aluminum Nitride by Nitridation of Γ-Al2o3 Nanoparticles in Flowing Ammonia

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Sulfur-assisted Fabrication of Silicon Nitride Nanorods in Autoclaves at 250 °C

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Synthesis of hexagonal monocrystal AlN microtubes and nanowires at low temperature

Nanosized Aluminum Nitride Hollow Spheres Formed Through a Self-Templating Solid–gas Interface Reaction

Synthesis of Monocrystal Aluminum Nitride Nanowires at Low Temperature

Synthesis of Aluminum Nitride Nanocrystals and Platelets

Synthesis of Pure Hexagonal Phase Aluminium Nitride Foam

Controllable Synthesis of One-Dimensional Aluminum Nitride Nanostructures Through Vapor-Solid Epitaxial Growth

Facile synthesis of monodisperse aluminum nitride microspheres

Study on the mechanism of aluminum nitride synthesis by chemical vapor deposition

Synthesis of AlN nanocrystalline powders