Abstract:Organic thin film transistor (OTFT) with a simplified planar structure is described. The gate electrode and the source/drain electrodes of OTFT are processed in one planar structure. And these three electrodes are deposited on the glass substrate by DC sputtering technology using Cr/Ni target. Then the electrode layouts of different width length ratio are made by photolithography technology at the same time. Only one step of deposition and one step of photolithography is needed while conventional process takes at least two steps of deposition and two steps of photolithography. Metal is first prepared on the other side of glass substrate and electrode is formed by photolithography. Then source/drain electrode is prepared by deposition and photolithography on the side with the insulation layer. Compared to conventional process of OTFTs, the process in this work is simplified. After three electrodes prepared, the insulation layer is made by spin coating method. The organic material of polyimide is used as the insulation layer. A small molecular material of pentacene is evaporated on the insulation layer using vacuum deposition as the active layer. The process of OTFTs needs only three steps totally. A semi-auto probe stage is used to connect the three electrodes and the probe of the test instrument. A charge carrier mobility of 0.3 cm2/V s, is obtained from OTFTs on glass substrates with and on/off current ratio of 105. The OTFTs with the planar structure using simplified process can simplify the device process and reduce the fabrication cost. © 2009 SPIE.

Low Temperature Organic Thin-Film Transistor Based On Tantalum Pentoxide Prepared By Anodization

Improved Photostability of Organic Thin Film Transistors with Tantalum Oxide/Poly(4-Vinylphenol) Double Gate Insulators

Pentacene Thin-Film Transistors with Ta2o5 As the Gate Dielectric

Nanocluster-Based Ultralow-Temperature Driven Oxide Gate Dielectrics for High-Performance Organic Electronic Devices

Low-Temperature Solution-Processed Gate Dielectrics for High-Performance Organic Thin Film Transistors

Planar Nanoscale Architecture for Organic Thin-Film Field-Effect Transistors

Low-Voltage Pentacene Thin-Film Transistors with Ta2o5 Gate Insulators and Their Reversible Light-Induced Threshold Voltage Shift

Thermally Stable Organic Thin Film Transistors Based on 2-(Anthracen-2-yl)tetracene

High-Performance Ultra-Low-Power OFET Based on Anodized TiOx Dielectric and Solution-sheared Organic Single Crystal

Improved Performance of Organic Thin Film Transistor with an Inorganic Oxide/Polymer Double-Layer Insulator

Improved Performance Of P-Type Pentacene Thin Film Transistor By Inserting Thin Interlayer Of N-Type Organic Semiconductor

Low-voltage high-performance C60 thin film transistors via low-surface-energy phosphonic acid monolayer/hafnium oxide hybrid dielectric

Low-voltage Organic Field-Effect Transistors Based on Novel High-Κ Organometallic Lanthanide Complex for Gate Insulating Materials

Fabrication of Indium-Tin-Oxide Thin-Film Transistor Using Anodization

Vertical Organic Thin-Film Transistor with Anodized Permeable Base for Very Low Leakage Current

Organic thin film transistor with a simplified planar structure

Polysiloxane-Poly(Vinyl Alcohol) Composite Dielectrics For High-Efficiency Low Voltage Organic Thin Film Transistors

The Interface Modification of Low-Voltage Pentacene-Based Organic Phototransistors

Pentacene organic thin-film transistors on flexible paper and glass substrates

Ultrahigh Mobility and Efficient Charge Injection in Monolayer Organic Thin-Film Transistors on Boron Nitride.

Ba0.6Sr0.4TiO3 Thin Films Used As Gate Dielectric in Pentacene Transistors