Enhance the Performance of CZTSSe Solar Cells Through Inhibiting the Cu2+, Tu, and (─COOH) Association Reaction
Lei Wang,Letu SiQin,Yiming Wang,Shuyu Li,Wenjing Xin,Jingyuan Guo,Ruijian Liu,Hongmei Luan,Chengjun Zhu
DOI: https://doi.org/10.1002/smll.202405908
IF: 13.3
2024-10-03
Small
Abstract:In this investigation, the influence of aging time on Cu2ZnSnS4 precursor solutions is assessed, revealing an association reaction among Cu2+, thiourea, and carboxyl groups. The incorporation of hydrochloric acid inhibits this reaction, diminishes the concentration of VSn(−/0) and CuSn(−/0) defects, and mitigates the band‐tailing effect, thereby attaining an optimal efficiency of 11% in a Cu2++Sn2+ system without MgF2. The Sol‐gel precursor solution reaction mechanism has a significant impact on the Cu2ZnSn(S, Se)4 (CZTSSe) solar cells. It is discovered that in the Cu2ZnSnS4 (CZTS) precursor solution (CZTS‐PS) in the preparation, there is an association reaction among Cu2+, thiourea (Tu), and carboxyl (‐COOH), which is an important reason for the undesirable CZTSSe solar cells. The strong association reaction generates excessive Cu2+ ions, forming the CuxSe secondary phase on the surface of the CZTSSe absorber. The secondary phase causes a short circuit and deterioration of gadget performance. Following a 6‐h aging period for the CZTS‐PS, the average photoelectric conversion efficiency (PCE) of the device is enhanced to 8.02%, and there is also an improvement in device uniformity, as evidenced by a decrease in the standard deviation to less than 1. To inhibit the association reaction and eliminate the aging time phenomenon, a strategy is developed using hydrochloric acid to regulate the CZTS‐PS environment. This strategy shifts the REDOX reaction in Cu2++Sn2+ toward the formation of Cu1++Sn4+, leading to a decrease in the defect concentrations of VSn(−/0) and CuSn(−/0), which increases the carrier concentration and reduces the impact of band tailing. The average power conversion efficiency (PCE) of the devices improved from 7.45% to 9.26%, the PCE of the best‐performing CZTSSe solar cells increased from 9.25% to 9.83%, and the consistency among the devices is further enhanced, as indicated by a reduction in the standard deviation from 0.98 to 0.44. Ultimately, the device performance of the Cu2++Sn2+‐DMF system improved by 11.01% (without the MgF2 layer) after optimization. This study serves as a reference for regulating the environment of the CZTS‐PS to further enhance the CZTSSe devices' performance, and the photoelectric conversion efficiency is improved by ≈30%.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology