Abstract:It is proved that secondary phases, such as Cu2Se, and ZnSe etc., and MoSe2 layer can form at Cu2ZnSn(S,Se)4 (CZTSSe)/Mo electrode interface, due to that Mo electrode reacts with CZTSSe and Se vapor during selenization process. The secondary phases and MoSe2 with inappropriate thickness can decrease power conversion efficiency (PCE) of CZTSSe solar cell. In this work, a simple method was proposed to suppress the reaction between CZTSSe and Mo, and to optimize the thickness of MoSe2. This was achieved by growing a layer of Mo oxide in situ on the Mo electrode surface through soaking the Mo electrode in H2O2. The Mo oxide layer consisted of MoO3, MoOx and MoO2. It could suppress the reaction between Mo and CZTSSe, thus preventing the formation of secondary phases in CZTSSe. By further tuning the soaking time, the thickness and density of the Mo oxide layer were optimized, resulting in an optimized thickness of the MoSe2 layer and a significant improvement in the contact quality at both the front and back interfaces. This improvement is beneficial for suppressing carrier recombination and reducing contact resistance. Furthermore, the Cu/(Zn+Sn) ratio in CZTSSe was optimized, leading to an expansion of the depletion region width. As a result, the reverse saturation current density and series resistance decrease, while the photogenerated current density increases. This ultimately led to a rise in PCE from 7.66% for CZTSSe solar cells with Mo electrodes that were not soaked to 8.95% for those with Mo electrodes soaked for 20 s.

Optimization of DMSO-based Precursor Solution by H2O Additive for Performance Enhancement of Kesterite Photovoltaic Devices

A DMSO/MOE mixed solvent system for improving the morphology and efficiency of kesterite solar cell

Precursor Solution Chemistry Via Water Additive Enabling CZTSSe Solar Cells with over 12％Efficiency

Improved CZTSSe Thin-Film Morphology and Device Performance by Using DMSO/DMF Blended Solvent

Enhancing the performance of CZTSSe solar cells via an alternate spin-coating process with DMSO and DMF

Enhancement of Cu2ZnSn(S, Se)4 device performance using an IPA/MOE hybrid solvent system in ambient air

Promoting Carrier Collection by DMF/DMSO Binary Solvent for Efficient Kesterite Solar Cells

Regulating Hetero‐Nucleation Enabling Over 14% Efficient Kesterite Solar Cells

Improvement of the Photovoltaic Performance of Cu2ZnSn(SxSe1-x)(4) Solar Cells by Adding Polymer in the Precursor Solution

Improvement of Cu2 ZnSn(S,Se)4 Solar Cells by Adding N,N-Dimethylformamide to the Dimethyl Sulfoxide-Based Precursor Ink.

Improvement of Cu2ZnSn(S,Se)4 Solar Cells by Adding N,N‐Dimethylformamide to the Dimethyl Sulfoxide‐Based Precursor Ink

Construction of a Low-Resistivity Carbon Layer to Improve Performance in Dimethyl Sulfoxide-Based Kesterite Solar Cells.

Performance Improvement of Cu2ZnSn(S,Se)4 Solar Cells by Ultraviolet Ozone Treatment on Precursor Films

Kesterite Cu2ZnSnS4 thin film solar cells by a facile DMF-based solution coating process

Enhancement of Power Conversion Efficiency of Cu2ZnSn(S,Se)4 Solar Cells by Pretreating Mo Electrode with H2O2

Suppressing Surface and Bulk Effect Enables High Efficiency Solution-Processed Kesterite Solar Cells

Improvement of Efficiency in Kesterite Solar Cells by Intentionally Inserting a Thin MoS2 Layer into the Back Interface.

Influencing Mechanism of Cationic Ratios on Efficiency of Cu2ZnSn(S,Se)(4) Solar Cells Fabricated with DMF-based Solution Approach

Coordination Engineering of Cu-Zn-Sn-S Aqueous Precursor for Efficient Kesterite Solar Cells

Novel non-hydrazine solution processing of earth-abundant Cu2ZnSn(S,Se)4 absorbers for thin-film solar cells

Using Cu–Zn–Sn–O Precursor to Optimize CZTSSe Thin Films Fabricated by Se Doping With CZTS Thin Films