Abstract:The brazed joint of sapphire transparent ceramic and Kovar alloy was prepared using AgCuTi and AgCuTiB composite filler, and the main focus was the effect of B element on the wetting behavior, interface composition and joint mechanical performance. The reliable joint of sapphire transparent ceramic and Kovar alloy was obtained by vacuum brazing with AgCu28-6Ti-0.45B (wt%) composite filler. The typical interfacial structure of the joint brazed at 825 °C for 10 min was determined as sapphire/Ti 3 Cu 3 O/Ag(s,s) + Cu(s,s) + disperse TiB/TiFe 2 + TiNi 3 /Kovar. The results showed that the addition of B could contributed to an optimized interfacial structure via (i) in-situ forming fine TiB whisker reinforcement phase and refining the interface structure and (ii) reducing the diffusion degree of alloy side elements to inhibit the generation of brittle phase, and the maximum shear strength of the joint with AgCu28-6Ti-0.45B (wt%) reached 125 MPa more than twice the joint without B additive. On the other hand, the wetting experiment showed that the addition of B as a solid particle decreased the fluidity of the composite filler, and when the addition of B was excessive, no dense TiB whiskers were produced in the interface. This study provides ideas for the optimization and improvement of sapphire composite connection, and points out that the generation of reinforcing phase is accompanied by the reduction of fluidity, so it is necessary to reasonably control the proportion of reinforcing phase.

Microstructure and Mechanical Property of Sapphire Joints Reinforced Byal4b2o9 Whiskers

New Design of Sapphire Joints Brazed with Bismuth-Borate Glass

Crystallization Behaviour of 25bi2o3–75b2o3 Glass Braze and Strengthening Mechanism of Crystallization-Reinforced Sapphire/25bi2o3–75b2o3/sapphire Joints

Microstructure and Characterization of Interfacial Phases of Sapphire/sapphire Joint Bonded Using Bi2O3–B2O3–ZnO Glass

Bismuth Borate Zinc Glass Braze for Bonding Sapphire in Air

Microstructural Evolution, Mechanical Properties, and FEM Analysis of the Residual Stress of Sapphire Joints Brazed with a Novel Borate Glass

Bonding Sapphire in Air by Using Bi2O3–B2O3 Glass Braze

Microstructure and Mechanical Performance of Composite Joints of Sapphire by Ultrasonic-Assisted Brazing

Joining Alumina And Sapphire By Growing Aluminium Borate Whiskers In-Situ, And The Whiskers' Orientation Relationship With The Sapphire Substrate

Bonding Layer Microstructures and Mechanical Behavior of Sapphire/Sapphire Joints Diffusion-Bonded Using Mgo-Al2o3-Sio2 Interlayer

Crystallization and Wetting Behavior of Bismuth–borate–zinc Glass and Its Application in Low Temperature Joining Alumina Ceramics

Air-brazed Al2O3 Joint with a Novel Bismuth Glass

Ultrasonic-assisted brazing of sapphire with high strength Al–4.5Cu–1.5Mg alloy

Low-temperature Brazing of Alumina Ceramics with Bismuth-Borate Glass in Air

Microstructure evolution and cooperative reinforcement mechanisms of Al2O3/Al2O3 joints brazed by low-melting borosilicate glass

Improvement of microstructure and mechanical properties of Sapphire/Kovar alloy joints brazed with Ag-Cu-Ti composite filler by adding B powders

Heterogeneous material joining of sapphire and TC4 alloy with a functionally graded interface

Interfacial Microstructure and Mechanical Properties of Titanium/Sapphire Joints Brazed with AuSn20 Filler Metal

Microstructure Evolution and Mechanical Properties of Znal2o4-Reinforced Al2o3/Al2o3 Joints Brazed with A Bismuth Borate Zinc Glass

Novel design of sapphire/spinel transparent ceramic joints with double glass interlayers by coating and bonding

Microstructure evolution and mechanical properties of YAG/YAG joint using bismuth-borate glass