Low-temperature Brazing of Alumina Ceramics with Bismuth-Borate Glass in Air
Wei Guo,Li Fu,Peng He,Tiesong Lin,Zhikang Shen,Xiao Chao Liu,Tong Wang,Chunyue Wang
DOI: https://doi.org/10.1016/j.matchar.2019.01.020
IF: 4.537
2019-01-01
Materials Characterization
Abstract:Bismuth-borate glass having a chemical composition of 50MBi(2)O(3)-50B(2)O(3) (mol.%), was designed and used to join alumina ceramics (95Al(2)O(3)) in air. Prior to brazing process, the wettability of the glass on 95Al(2)O(3) was investigated, and the results showed good wettability of the glass/95Al(2)O(3) system. Subsequently, 95Al(2)O(3) was brazed at temperatures ranging from 600 to 700 degrees C, sound joints free of defects were obtained. Al4B2O9 was formed in the joints due to a reaction between B2O3 from the glass and 95Al(2)O(3). The formation of Al4B2O9 in the joint domain could reduce the thermal expansion coefficients (CTEs) mismatch between 95Al(2)O(3) and glass, which is benefit for the release of the internal stress in the joint. Microstructure evolution and mechanical properties of the joint versus temperature were investigated. The results showed that with the increase in brazing temperature, the size of Al4B2O9 increased, meanwhile, the infiltration of the glass into 95Al(2)O(3) was more and more serious. With brazing temperature increasing, the three-point bending strength of the joint first increased and then decreased. The optimal joint strength of 188 MPa was acquired when the sample was brazed at 625 degrees C for 20 min.