Abstract:Vacuum brazing of TC4 alloy and SiO2 ceramic was achieved using a nano-AgCuNi braze alloy. The melting temperature of nano-AgCu powders was analyzed by differential scanning calorimeter. Furthermore, the effects of the Ni content on the microstructure and mechanical properties of the joints were studied. The results showed that the melting temperature of the nano-AgCu filler was 774 °C. A decrease in the melting temperature of 6 °C was observed, compared with the general AgCu filler, and this decrease enabled the interfacial reaction of the joint to begin earlier. The typical interfacial microstructure of the TC4/nano-AgCuNi/SiO2 ceramic joint brazed at 950 °C for 10 min was TC4/α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectoid structure/Ti2(Cu,Ni) compound with α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectic structure/Ti4O7 + TiSi2/SiO2 ceramics. The homogeneous microstructure of α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectoid structure primarily existed in the diffusion layer. Additionally, the refined α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectic structure created via a eutectic reaction and Ti2(Cu,Ni) compound was distributed in the brazing seam. The Ni content could influence the formation of Ti-Cu-Ni ternary intermetallic compounds (IMCs). An increase in Ni led to an increase in the α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectic structure in the brazing seam. The shear strength of the brazed joints first increased and then decreased with the increase in the nano-Ni content, and the optimal shear strength of 30.1 MPa was achieved at 10 wt.% Ni. The increase in the α-Ti + Ti2(Cu,Ni) + Ti2(Ni,Cu) hypereutectic structure and the decrease in brittle compounds enhanced the shear strength of the joint. Fracture analysis of the joints brazed at 950 °C for 10 min indicated that the cracks mainly occurred in SiO2 ceramic.

Microstructure and Fracture Behavior of SiO 2 Glass Ceramic and TC4 Alloy Joint Brazed with TiZrNiCu Alloy

Active brazing of SiO_2 glass ceramic to TC4 alloy

Research on the Brazing of SiO_2 Ceramic to TC4 Alloy

Interface microstructure and mechanical properties of the brazed SiO2 glass ceramic and 30Cr3 high-tensile steel joint

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Effects of processing parameters on microstructure and mechanical behavior of SiO2/Ti–6Al–4V joint brazed with AgCu/Ni interlayer

Microstructure and Mechanical Property of Vacuum Brazed SiC Ceramic Joint

Interface Evolution of SiO2 Glass Ceramic and Ti–6Al–4V Alloy Joint Brazed with Ag–Cu–Ti Alloy

Research on the interfacial structure and mechanical properties of TC4-SiO2 composite brazed joint

Microstructure and Mechanical Properties of a SiO2 Ceramic and TC4 Alloy Joint Brazed with a Nanocomposite Filler

Microstructure Evolution and Bonding Mechanism of ZrO2 Ceramic and Ti-6Al-4V Alloy Joints Brazed by Bi2O3-B2O3-ZnO Glass Paste

Interface microstructure and mechanism of SiC ceramic vacuum brazed joint

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

Understanding the Microstructure Evolution Mechanism and the Microstructure-Strength Correlations of Ti3SiC2/Ti2AlNb Joint Brazed with AgCu Interlayer

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Interfacial Reaction Behavior and Mechanical Characterization of ZrO2/TC4 Joint Brazed by Ag–Cu Filler Metal

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

Microstructure and mechanical response of the SiO2f/SiO2 composite and Invar alloy joints brazed with an AgCuTi alloy

Effect of brazing temperature on interfacial microstructure and mechanical property of Ti60/AgCu/ZrO2 joint

Microstructural Evolution and Mechanical Properties of Zrb2-Sic/Cu/Ti/Ti6al4v Brazing Joints

Interfacial Microstructure and Mechanical Property of Brazed Copper/sio2 Ceramic Joint