Interface Evolution of SiO2 Glass Ceramic and Ti–6Al–4V Alloy Joint Brazed with Ag–Cu–Ti Alloy

H. B. Liu,L. X. Zhang,D. Liu,P. He,J. C. Feng

DOI: https://doi.org/10.1179/026708309x12506933873026

IF: 1.8

2011-01-01

Materials Science and Technology

Abstract:In the present paper, SiO2 glass ceramic was joined to Ti–6Al–4V alloy with 35Ti–35Zr–10Ni–15Cu (wt-%) filler foil. The whole brazing process was performed under vacuum circumstances at different temperatures (850–1000°C) for several holding times (1–30 min). According to results of scanning electron microscopy, energy dispersive spectrometry, electron probe X-ray microanalysis and X-ray diffraction analysis, the reaction products of the interface are Ti2O, Zr3Si2, Ti5Si3, Ti based solid solution and Ti2(Cu,Ni). There is residual TiZrNiCu braze alloy on the SiO2 glass ceramic/Ti–6Al–4V alloy interface after brazing. Besides, the interface evolution model of the joint was described by four stages: diffusion and solution among atoms, formation of reaction products, precipitation and growth of reaction layers respectively.