Abstract:Due to the poor wettability of the AgCuTi alloy on the SiO2f/SiO2 composite, direct brazing of the composite with an Invar alloy could hardly achieve a reliable joint. To overcome that, the SiO2f/SiO2 composite was decorated with few-layer graphene (FLG) by a plasma enhanced chemical vapor deposition (PECVD) method. Sessile drop experiments indicate that the contact angle dropped from 123.8° to 50.7° after FLG was grown on the surface of the SiO2f/SiO2 composite. Afterwards, the effects of brazing temperature and Ti contents on the microstructure evolution and mechanical properties of joints (Invar/SiO2f–SiO2 modified with FLG) were investigated. The typical interface structure of the joint is SiO2f–SiO2/Ti5Si3+TiO2+CuxTi6−xO(x=2,3)/Ag(s,s)+Cu(s,s)+Cu–Ti blocks/wave-like Fe2Ti+Ni3Ti/Ag(s,s)+Cu(s,s)+Fe2Ti+Ni3Ti blocks/Invar. As the brazing temperature and Ti contents increase, the reaction layer on the SiO2f/SiO2 side becomes thicker and cracks gradually propagate. Meanwhile, a few dispersive Fe2Ti+Ni3Ti phases change into large-area wave-like compounds and more Cu–Ti compounds form with the increase of the Ti content. The microstructure evolution significantly affects the shear strength of the brazed joints. The highest shear strength is 26MPa brazed at 860°C for 10min with 4.5wt.% Ti content.

Microstructure and mechanical response of the SiO2f/SiO2 composite and Invar alloy joints brazed with an AgCuTi alloy

Brazing of SiO 2f /SiO 2 composite modified with few-layer graphene and Invar using AgCuTi alloy

Effects of processing parameters on microstructure and mechanical behavior of SiO2/Ti–6Al–4V joint brazed with AgCu/Ni interlayer

Research on the interfacial structure and mechanical properties of TC4-SiO2 composite brazed joint

Microstructure and Mechanical Properties of Invar Alloy and Si3N4 Ceramic Brazed Joints

Interfacial Microstructure and Mechanical Property of SiO2-BN Ceramics and Invar Joint Brazed with Ag–Cu–Ti Active Filler Metal

Microstructural Evolution of Si3n4/Ti6al4v Joints Brazed with Nano-Si3n4 Reinforced Agcuti Composite Filler

Microstructure and Mechanical Properties of SiO2-BN Ceramic and Invar Alloy Joints Brazed with Ag–Cu–Ti+TiH2+BN Composite Filler

Correlation between microstructure and mechanical properties of active brazed Invar/SiO 2-BN joints

Microstructure and mechanical properties of the joint between Si3N4 and Mo brazed by near‐eutectic Ag‐Cu‐In‐Ti filler alloy

Brazing SiO2f/SiO2 Composite to Invar Alloy Using a Novel TiO2 Particle-Modified Composite Braze Filler

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Research on the Interfacial Structure and Properties of TiAl - Si3N4f/Si3N4 Brazed Joints

Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler

Understanding the Microstructure Evolution Mechanism and the Microstructure-Strength Correlations of Ti3SiC2/Ti2AlNb Joint Brazed with AgCu Interlayer

Brazing of SiO2f/SiO2 Composite to Invar Using a Graphene-Modified Cu-23Ti Braze Filler

Microstructural Evolution and Mechanical Properties of the Joint of TiAl Alloys and C/SiC Composites Vacuum Brazed with Ag–Cu Filler Metal

Microstructure and Fracture Behavior of SiO 2 Glass Ceramic and TC4 Alloy Joint Brazed with TiZrNiCu Alloy

Effect of brazing temperature on interfacial microstructure and mechanical property of Ti60/AgCu/ZrO2 joint

Microstructure Evolution and Brazing Mechanism of Ti5Si3/Ti3Al Composite and Ni-based Superalloy Joints Using Ti-Zr-Cu-Ni Filler Alloy

Active Brazed Invar-SiO2f/SiO2 Joint Using a Low-Expansion Composite Interlayer