Abstract:ZrO2 ceramic was metallized by Sn-xTi (x = 2, 3 and 4 at.%) foils at 1000 degrees C for 30 min. As the Ti content was 3%, the continuous and homogeneously distributed Ti-O compounds layer formed at the interface. The metal-lization layer metallized Sn-3Ti foil consisted of Ti2O3 layer + Ti11.31Sn3O10/beta-Sn + Ti2Sn3+Ti6Sn5. During the metallization process, as the thickness of metallization layer increased, the Ti-O and Ti-Sn-O layers became continuous, Ti2Sn3 and Ti6Sn5 phases increased and aggregated obviously. Vacuum brazing using AuSn20 filler metal after pre-metallization were utilized to achieve the robust ZrO2/Sn-3Ti/AuSn20/Ti joints. The effect of the metallization layer thickness on microstructure and mechanical properties was systematically examined. The typical interfacial microstructure of ZrO2/Sn-3Ti/AuSn20/Ti joints brazed at 550 degrees C for 30 min was ZrO2/ Ti2O3+Ti11.31Sn3O10/beta-Sn + Ti6Sn5+AuSn2+AuSn4+AuTi5Sn3 layer/Ti. During brazing process, the Ti-O and Ti-Sn-O layers beside ZrO2 ceramic varied barely with the increasing of the thickness of metallization layer during brazing process. In the brazing seam, the AuSn2 phases and Ti6Sn5 phases attenuated whereas AuSn4 phases evidently increased with the thicker metallization layer. The AuTi5Sn3 layer nearby the Ti substrate thickened significantly varied with the thickness of metallization layer. Additionally, the ZrO2/Ti brazed joint with the maximum shear strength of 48.6 MPa was achieved by the metallization layer thickness of 150 mu m. Furthermore, fracture analysis demonstrated that the cracks initiated at the Ti-O layer and propagated along the AuSn2 phases and layered Au-Ti-Sn phases.

Interfacial Microstructure and Mechanical Properties of Titanium/Sapphire Joints Brazed with AuSn20 Filler Metal

Microstructure and Mechanical Property of Titanium Film-Modified Sapphire/High Nb-TiAl Alloy Joints Using Ag-Cu Filler by Vacuum Brazing

Microstructure and Mechanical Performance of Composite Joints of Sapphire by Ultrasonic-Assisted Brazing

Low Temperature Brazing of Biomedical Titanium and Zirconia Metallized with Sn-Ti Metal Foil

Evaluation of Biomedical Ti/ZrO2 Joint Brazed with Pure Au Filler: Microstructure and Mechanical Properties

Evolution of Interfacial Structures and Mechanical Performance of Sapphire and Sn–9Zn–2Al Joints by Ultrasound

Low Temperature Brazing Between Pre-Metallized ZrO2 Ceramics and Medical Pure Titanium Using AuSn20 Filler Metal

Interfacial microstructure and properties of Ti53311S titanium alloy joints brazed using TiZrNiCu filler metal

Microstructure Evolution and Mechanical Properties of Titanium/Alumina Brazed Joints for Medical Implants

Interfacial microstructure and mechanical properties of ZTA/ZTA joints brazed with Ni-Ti filler metal

Microstructure and Characterization of Interfacial Phases of Sapphire/sapphire Joint Bonded Using Bi2O3–B2O3–ZnO Glass

Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler

Research on the Interfacial Structure and Properties of TiAl - Si3N4f/Si3N4 Brazed Joints

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2

Effect of brazing temperature on interfacial microstructure and mechanical property of Ti60/AgCu/ZrO2 joint

Microstructural Evolution of Si3n4/Ti6al4v Joints Brazed with Nano-Si3n4 Reinforced Agcuti Composite Filler

Interfacial Microstructure and Mechanical Properties of TC4 Titanium Alloy/316L Stainless Steel Joint Brazed with Ag70.5Cu27.5Ti2 Filler Metal

Interfacial Microstructure and Properties of In-situ TiB Reinforced ZrB2-SiC Joints

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Interfacial microstructure and performance of nano-diamond film/Ti-6Al-4V joint brazed with AgCuTi alloy

Microstructure Evolution of TC4 Titanium Alloy/316l Stainless Steel Dissimilar Joint Vacuum-Brazed with Ti-Zr-Cu Amorphous Filler Metal