Abstract:Reducing the residual stresses and improving the mechanical strength of large-scale ceramic/metal brazing joints is an important problem that must be solved for its practical engineering application. Using composite filler with solid-state phase transformation ceramic particulates, it is theoretically feasible to relieve the residual stress and improve the mechanical properties of ceramic/metal brazed joints. In this study, Cu mesh, Ag-28Cu-2Ti (wt.%), and YSZ (0.6 mol.% Yttria-stabilized Zirconia solid-state phase transformation ceramic particulates) composite power fillers were used in the brazing of Ti3SiC2 ceramic and pure copper. The microstructure of joints and YSZ particulates in the interface was investigated and confirmed by SEM, EDS, STEM and TEM. In addition, the effect of YSZ particulates content on the mechanical properties of joints was investigated and evaluated by the shear strength. The results show that the interfacial phases were mainly Ti5Si3, TiC, TixCu, Ag (s, s), Cu (s, s) and YSZ particulates. Moreover, most of YSZ particulates undergo the solid-state phase transformation from t-ZrO2 to m-ZrO2 during the cooling process of brazing. The abnormal volume expansion of the solid-state phase transformation reduced the thermal mismatch between Ti3SiC2 ceramic and filler, thereby reducing the residual stress in the interface of joint. When using composite filler with 6wt.% YSZ particulates, the shear strength of Ti3SiC2/Cu joint reached the maximum. The maximum average shear strength of the joints was 80.2 MPa, which was about 103.6% more than the joint without YSZ particulates.This article is protected by copyright. All rights reserved

Nano particle reinforced Ag-base composite brazing filler metal and preparation method thereof

Microstructure and mechanical properties of brazing joint of silver-based composite filler metal

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Reactive composite brazing of C/C composite and GH3044 with Ag–Ti mixed powder filler material

Si3N4 Ceramics Brazing with Composite Soldering Materials

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Achieving ultrafine grain strengthening C f /SiC-GH3536 joints brazed with Cu-Ti-WC composite interlayer via cold spray additive manufacturing

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Influence of microalloying with B on the microstructure and properties of brazed joints with Ag–Cu–Zn–Sn filler metal

Investigation on the microstructure, mechanical and electrical properties of Ti3SiC2/Cu joint obtained by Ti25Zr25Ni25Cu25 amorphous high entropy alloy and Ag composite filler

A novel high entropy CoFeCrNiCu alloy filler to braze SiC ceramics

Graphite-reinforced AgCuTi/Cu foam composite filler to braze Al2O3 ceramic and 304 stainless steel

Joint Microstructure and Performance of Brazing Si3N4‐MoSi2 Composites to Nb with AgCuTi and AgCuTi+MoSi2p Active Fillers

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Microstructure and mechanical properties of the joint between Si3N4 and Mo brazed by near‐eutectic Ag‐Cu‐In‐Ti filler alloy

Effect of Ti content on microstructure and mechanical properties of SiCf/SiC composites/GH536 superalloy joints brazed with CoFeCrNiCuTi high entropy filler

Interfacial Bonding Mechanism and Joint Weakness Area of Brazed SiC and Nb with AuNi Filler Alloy: First‐principles and Experimental Perspective

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

A novel CoCrNi medium entropy alloy enhanced AgCuTi composite filler to braze Kovar alloy and sapphire

Preparation method of carbon nano tube enhanced copper-based composite material