Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Synthesis of SiC-TiC Composite Powders Using Glucose as Carbon Source

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Synthesis of nanocrystalline silicon carbide powders

Rapid Synthesis of SiC Powders by Spark Plasma-Assisted Carbothermal Reduction Reaction

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Combustion synthesis of SiC/Al2O3 composite powders with SiC nanowires and their growth mechanism

Combustion Synthesis of Ti<sub>3</sub>SiC<sub>2</sub>/TiC Composites from Elemental Powders under High-Gravity Conditions

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Synthesis of Ti(C,N) ultrafine powders by carbothermal reduction of TiO2 derived from sol–gel process

Controlled growth of SiC crystals in combustion synthesis

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Combustion synthesis of (TiC+SiC) composite powders by coupling strong and weak exothermic reactions

Exploring the impact of pH and temperature on TiC nanopowders syntesized via sol-gel and subsequent crystallization by carbothermal reduction method

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Preparation of β-Sialon /SiC composite powder by carbothermal reaction of coal-mine schist

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Synthesis and characterization of submicron silicon carbide powders with silicon and phenolic resin

Direct Synthesis of Controllable Microstructures of Thermally Stable and Ordered Mesoporous Crystalline Titanium Oxides and Carbide/Carbon Composites