Abstract:Herein, a stable LiNbO3 (LN) sol, with different Zn2+ contents, is prepared using ethanol niobium, lithium acetate and zinc acetate as starting materials, absolute ethanol as a solvent, and acrylic acid and benzoyl acetone (BzAcH) as additives. The influence of Zn2+ content on LN crystal structure, light transmittance and J-V curve characteristics is studied in detail. XRD results reveal that Zn2+ doping, with a molar content of less than 5%, does not influence the crystal structure of LN. SEM indicates that the grain size of LN films gradually increases with the increase of doping content. The surface quality of LN films becomes worse when the doping content of Zn2+ reaches 5%. Moreover, light transmittance tests show that the maximum light transmittance is attained at the doping amount of 3%. J-V curves demonstrate that Pt/LN/LNO(LaNiO3) structure shows excellent resistance switching (RS) effect due to the formation of Schottky barrier at the Pt/LN interface, which initially becomes prominent with the increase of Zn2+ content, followed by a gradual decrease. On the other hand, In/LN/LNO structure exhibits poor RS effect due to the unobvious Schottky barrier at In/LNO interface. Furthermore, J-V curves at different temperatures demonstrate that the RS effect of Pt/LN/LNO structure tends to deteriorate, while the refractive index of LN film increases with the decrease of temperature. Herein, the abovementioned RS phenomenon is analyzed and explained in terms of the relationship between interfacial barrier and doping amount of Zn2+, migration of oxygen vacancies, and the relationship between insulation property of LN films and temperature. The research results are of experimental and theoretical significance for practical applications of LN films.

Fabricate and Characterize the Lithium Niobate Thin Films Prepared on Glass Substrate by Sol-gel Process

Preparation and characterization of LiNbO3 thin films derived from metal carboxylate gels

Preparation and Characterization of LiNbO<sub>3</sub> Thin Films Derived from Metal Carboxylate Gels

LiNbO3 Thin Films through a Sol–Gel/Spin-Coating Approach Using a Novel Heterobimetallic Lithium–Niobium Precursor

Preparation of LiNbO3 Films on Si( 111 ) Substrates by a Modified Sol-Gel Process

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Preparation and Properties of NiO Films Via Sol-gel Process and Spin-coating

Characterization of Lithium Niobate Thin Films Derived from Aqueous Solution

RESEARCH ON THE LiNbO3 THIN FILMS PREPARED BY SOL-GEL PROCESS

Preparation And Properties Of Nb2o5-Fe2o3 Sol-Gel Optical Films

Patterning of Lithium Niobate Thin Films Derived from Aqueous Solution

Deposition of stress free c-axis oriented LiNbO3 thin film grown on (002) ZnO coated Si substrate

Characteristics of the precursors and their thermal decomposition during the preparation of LiNbO3 thin films by the Pechini method

Fabrication of the preferentially orientated LiNbO3 nanoparticles and their ferroelectric behaviors

Preparation and Characterization of LiTaO 3 Films Derived by an Improved Sol-Gel Process

GROWTH AND CHARACTERIZATION OF C-ORIENTED <font>LiNbO</font><sub>3</sub> THIN FILMS ON Si (100) BY PLD

Microstructure of LiNbO3 Thin Films Grown on Silicon Substrates by Pulsed Laser Deposition

GROWTH AND CHARACTERIZATION OF C-ORIENTED LiNbO3 THIN FILMS ON Si (100) BY PLD

J-V characteristics of sol-gel-prepared Zn2+ doped LiNbO3

Fabrication and Conductive Characteristic of Highly Oriented Lanio3 Thin Films