Abstract:Crystal growth of barium titanate (BaTiO3) using a wet chemical reaction was investigated at various temperatures. BaTiO3 nanoparticles were obtained at an energy-efficient temperature of 80 °C. However, BaTiO3 nanocubes with a preferred size and shape could be synthesized using a solvothermal method at 200 °C via a reaction involving titanium tetraisopropoxide [(CH3)2CHO]4Ti for nucleation and fine titanium oxide (TiO2) nanoparticles for crystal growth. The BaTiO3 nanocubes showed a high degree of dispersion without the use of dispersants or surfactants. The morphology of BaTiO3 was found to depend on the reaction medium. The size of the BaTiO3 particles obtained using water as the reaction medium was the largest among the particles synthesized using various reaction media. In the case of alcohol reaction media, the BaTiO3 particle size increased in the order methanol, ethanol, 1-propanol, 1-butanol, and 1-pentanol. Furthermore, BaTiO3 powder obtained using alcohol reaction media resulted in cubic shapes as opposed to the round shapes obtained when water was used as the medium. We found that the optimal condition for the synthesis of BaTiO3 nanocubes involved the use of 1-butanol as the reaction medium, resulting in an average particle size of 52 nm, which is the average distance of the cubes measured diagonally from corner to corner, and gives an average side length of 37 nm, and a tetragonal crystal system as evidenced by the powder X-ray diffraction pattern obtained using high-energy synchrotron X-rays. The origin of the spontaneous polarization of the BaTiO3 tetragonal crystal structure was clarified by a pair distribution function analysis. In addition, surface reconstruction of BaTiO3 nanocubes led to an outermost surface comprising two layers of Ti columns.

Tetragonality and size control of barium titanate nanopowders prepared by solvothermal method

Size-controllable barium titanate nanopowder synthesized via one-pot solvothermal route in a mixed solvent

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

A Facile and Eco-Friendly Hydrothermal Synthesis of High Tetragonal Barium Titanate with Uniform and Controllable Particle Size

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Preparation and Characterization of Monodispersed BaTiO3 Nanocrystals Using One-Step Solvothermal Method

Preparation of Monodisperse Nanocrystalline Barium Titanate

Fabrication of Monodispersed 5‐nm BaTiO3 Nanocrystals with Narrow Size Distribution Via One‐Step Solvothermal Route

Hydrothermal Synthesis of Tetragonal Barium Titanate Nanopowders under Moderate Conditions

Stabilization of Size-Controlled BaTiO3 Nanocubes via Precise Solvothermal Crystal Growth and Their Anomalous Surface Compositional Reconstruction

Synthesis of monodispersed barium titanate nanoparticles with narrow size distribution by a modified alkoxide-hydroxide sol-precipitation method

Preparation and characterizations of tetragonal barium titanate powders by hydrothermal method

Solvothermal synthesis and Curie temperature of monodispersed barium titanate nanoparticles

Experimental and Simulation-Based Understanding of Morphology Controlled Barium Titanate Nanoparticles under Co-Adsorption of Surfactants

Synthesis Of Tetragonal Batio3 Nano-Particle Via A Novel Tartaric Acid Co-Precipitation Process

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Synthesis and Performance of Tetragonal BaTiO3 Fine Powders Via a Facile Tartaric Acid Assisted Method

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Synthesis and Characterization of Tetragonal Barium Titanate Powders by an Ion-Exchange and Hydrothermal Process

Barium Titanate Tetragonal Prism Arrays: Preparation and Characterization