Abstract:Crystal growth of barium titanate (BaTiO3) using a wet chemical reaction was investigated at various temperatures. BaTiO3 nanoparticles were obtained at an energy-efficient temperature of 80 °C. However, BaTiO3 nanocubes with a preferred size and shape could be synthesized using a solvothermal method at 200 °C via a reaction involving titanium tetraisopropoxide [(CH3)2CHO]4Ti for nucleation and fine titanium oxide (TiO2) nanoparticles for crystal growth. The BaTiO3 nanocubes showed a high degree of dispersion without the use of dispersants or surfactants. The morphology of BaTiO3 was found to depend on the reaction medium. The size of the BaTiO3 particles obtained using water as the reaction medium was the largest among the particles synthesized using various reaction media. In the case of alcohol reaction media, the BaTiO3 particle size increased in the order methanol, ethanol, 1-propanol, 1-butanol, and 1-pentanol. Furthermore, BaTiO3 powder obtained using alcohol reaction media resulted in cubic shapes as opposed to the round shapes obtained when water was used as the medium. We found that the optimal condition for the synthesis of BaTiO3 nanocubes involved the use of 1-butanol as the reaction medium, resulting in an average particle size of 52 nm, which is the average distance of the cubes measured diagonally from corner to corner, and gives an average side length of 37 nm, and a tetragonal crystal system as evidenced by the powder X-ray diffraction pattern obtained using high-energy synchrotron X-rays. The origin of the spontaneous polarization of the BaTiO3 tetragonal crystal structure was clarified by a pair distribution function analysis. In addition, surface reconstruction of BaTiO3 nanocubes led to an outermost surface comprising two layers of Ti columns.

Fabrication of Monodispersed 5‐nm BaTiO3 Nanocrystals with Narrow Size Distribution Via One‐Step Solvothermal Route

Preparation and Characterization of Monodispersed BaTiO3 Nanocrystals Using One-Step Solvothermal Method

Synthesis of monodispersed barium titanate nanoparticles with narrow size distribution by a modified alkoxide-hydroxide sol-precipitation method

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Monodisperse Hollow Perovskite BaTiO3 Nanostructures Prepared by a Sol–gel–hydrothermal Method

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Preparation of Monodisperse Nanocrystalline Barium Titanate

Investigation on the Synthesis Procedure of Ultrafine Monodispersed BaTiO3 Powders by Solvothermal Method

Size Effect Investigation on Nano-Scale Ferroelectric Ceramic Materials

Stabilization of Size-Controlled BaTiO3 Nanocubes via Precise Solvothermal Crystal Growth and Their Anomalous Surface Compositional Reconstruction

Influence of Raw Material Ratio of Ba/Ti on Fabrication of Nanocrystalline Batio3 Powder

Fabricating Uniform Tetragonal Barium Titanate Nanocrystals Via Sand Milling Assisted by an Innovative Two-Step Calcination

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Rapid Formation of Nanocrystalline Batio3 and Its Highly Stable Sol

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method