Abstract:BaTiO3 (BT) nanoparticles were prepared by the hydrothermal technique using different starting materials and the microstructure examined by XRD, SEM, TEM and HRTEM. X-ray diffraction and electron diffraction patterns showed that the nanoparticles were the cubic BaTiO3 phase. The BT nanoparticles prepared from the starting materials of as-prepared titanium hydroxide and barium hydroxide have spherical grain morphology, an average size of 65 nm and a fairly narrow size distribution. A uniform diffraction contrast across each single grain is observed in the TEM images, and the clear lattice fringes (with d(110) = 0.28 nm) observed in HRTEM images reveal that well-crystallized BT nanoparticles are synthesized by the hydrothermal method. The edges of the particles are very smooth, with no surface steps. BT nanoparticles with average grain size of 90 nm, synthesized using barium hydroxide and titanium dioxide as the starting materials, show surface facets. In this case a bimodal size distribution of large faceted and smaller particles is observed. Diffraction contrast variation across the particles caused by high strains within the particles is clearly observed. The high strains obviously stem from structural defects formed during hydrothermal synthesis, presumable in the form of lattice OH- ions and their compensation by cation vacancies. HRTEM images demonstrate that surface facets parallel to the (100) and (110) planes and small islands with 3 similar to 4 atomic layer thickness are frequently observed around the edge of the particles.

Investigation on the Synthesis Procedure of Ultrafine Monodispersed BaTiO3 Powders by Solvothermal Method

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Preparation and Characterization of Monodispersed BaTiO3 Nanocrystals Using One-Step Solvothermal Method

Synthesis of monodispersed barium titanate nanoparticles with narrow size distribution by a modified alkoxide-hydroxide sol-precipitation method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Synthesis and Characterization of BaTiO3 Nanopowders Via Solvothermal Method

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Monodisperse Hollow Perovskite BaTiO3 Nanostructures Prepared by a Sol–gel–hydrothermal Method

Fabrication of Monodispersed 5‐nm BaTiO3 Nanocrystals with Narrow Size Distribution Via One‐Step Solvothermal Route

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Solvothermal synthesis, characterization and formation mechanism of single-crystalline SrTiO3 dense spheres with monoethanolamine as reaction medium solvent

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Preparation of Monodisperse Nanocrystalline Barium Titanate

Microstructural Characterization of BaTiO3 Ceramic Nanoparticles Synthesized by the Hydrothermal Technique