Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of Ni3Al-Bonded TiC-Based Cermets

Haifeng Luo,Weihao Xiong,Qingqing Yang,Man Zhang,Shan Chen,Shengqing Wang

DOI: https://doi.org/10.3969/j.issn.1003-7292.2017.04.004

2017-01-01

Abstract:Ni powder and Al powder were used to synthesize Ni3Al powder by mechanical alloying,and then Ni3Albonded TiC-based cermets with various Cr3C2 content were prepared by powder metallurgy route,including sintering under vacuum at 1 485℃ for 1 h.The research shows that the Ni3Al-bonded TiC-based cermets are composed of TiC cermet grains and Ni3Al binder phase,and the TiC cermet grains generally exhibit core-rim structure.When Cr3C2 content is 6wt.％,the number of the fine cermet grains with white core increases,and moreover white inner rim in the cermet grains with black core becomes more complete.The hardness and transverse rupture strength of the cermets firstly increase and then decrease with the increase of Cr3C2 content.The fracture toughness of the cermet firstly increases and then decreases,followed by slightly increases and decreases with the increase of Cr3C2 content.When Cr3C2 content is 2.0wt.％,the Ni3Al-bonded TiCbased cermets have good mechanical properties.